Multi-walled Carbon Nanotubes Content Research Articles

Multifunctionality of MWCNT and TiC hybrid filler silicone composite for energy harvesting and strain sensing

AbstractThe flexible silicone elastomer‐conductive composite was developed with enhanced energy harvesting and strain sensing. A hybrid nanofiller system with multi‐walled carbon nanotubes (MWCNTs) and titanium (IV) carbide (TiC) was used as reinforcing agents for the elastomer. The 4 MWCNT +5 TiC composite has 1.34 MPa tensile strength, 136.85% higher than unfilled silicone rubber (SR) matrix. The unfilled sample has a 1.558 MPa compressive modulus, while 4 MWCNT +5 TiC has 3.87 MPa. The machine and finger presses were utilized to test the energy harvesting of the composite. With greater cyclic stability, the 4 MWCNT +5 TiC sample performed exceptionally well in the machine press in the output voltage range of around 120 mV. Among the thumb presses, 2 MWCNT +5 TiC yielded the best results, with a voltage of about 100 mV. The 3 MWCNT +5 TiC sample produced 9044% more energy than the single filler 3 phr MWCNT sample from our previous work. Higher MWCNT content enhanced composite stiffness, making finger pressing harder and decreasing energy output. The strain sensing test on the 4 MWCNT +5 TiC composite showed high gauge factors (GF = 7.532 and 23.944) and good linearity (R2 = 0.909 and 0.939) over a strain range of Δε = 0%–14% and 14%–22%. Silicone composites' mechanical, energy harvesting, and strain sensing performance improved greatly with the MWCNT and TiC hybrid fillers. These composites could be used in self‐powered wearable electronics, machine or structural deformation monitoring, and human motion sensing.Highlights A stretchable device was developed with improved energy harvesting and strain sensing. Rubber composites were fabricated from MWCNTs, TiC hybrid fillers, and SR matrix. The energy harvesting was 9044% higher for hybrid filler compared to MWCNT as the only filler. Robust strain sensing properties with a gauge factor of 23.9, linearity of 0.91, and relaxation time of 0.1 s. The final composites are useful for self‐powered wearable electronics, health monitoring, and human motion sensing.

Characterization of airborne dust emissions from three types of crushed multi-walled carbon nanotube-enhanced concretes

Dispersing Multi-Walled Carbon Nanotubes (MWCNTs) into concrete at low (<1 wt% in cement) concentrations may improve concrete performance and properties and provide enhanced functionalities. When MWCNT-enhanced concrete is fragmented during remodelling or demolition, the stiff, fibrous and carcinogenic MWCNTs will, however, also be part of the respirable particulate matter released in the process. Consequently, systematic aerosolizing of crushed MWCNT-enhanced concretes in a controlled environment and measuring the properties of this aerosol can give valuable insights into the characteristics of the emissions such as concentrations, size range and morphology. These properties impact to which extent the emissions can be inhaled as well as where they are expected to deposit in the lung, which is critical to assess whether these materials might constitute a future health risk for construction and demolition workers. In this work, the impact from MWCNTs on aerosol characteristics was assessed for samples of three concrete types with various amounts of MWCNT, using a novel methodology based on the continuous drop method. MWCNT-enhanced concretes were crushed, aerosolized and the emitted particles were characterized with online and offline techniques. For light-weight porous concrete, the addition of MWCNT significantly reduced the respirable mass fraction (RESP) and particle number concentrations (PNC) across all size ranges (7 nm – 20 μm), indicating that MWCNTs dampened the fragmentation process by possibly reinforcing the microstructure of brittle concrete. For normal concrete, the opposite could be seen, where MWCNTs resulted in drastic increases in RESP and PNC, suggesting that the MWCNTs may be acting as defects in the concrete matrix, thus enhancing the fragmentation process. For the high strength concrete, the fragmentation decreased at the lowest MWCNT concentration, but increased again for the highest MWCNT concentration. All tested concrete types emitted <100 nm particles, regardless of CNT content. SEM imaging displayed CNTs protruding from concrete fragments, but no free fibres were detected.

Leveraging Oriented Lateral Walls of Nerve Guidance Conduit with Core-Shell MWCNTs Fibers for Peripheral Nerve Regeneration.

Peripheral nerve regeneration and functional recovery rely on the chemical, physical, and structural properties of nerve guidance conduits (NGCs). However, the limited support for long-distance nerve regeneration and axonal guidance has hindered the widespread use of NGCs. This study introduces a novel nerve guidance conduit with oriented lateral walls, incorporating multi-walled carbon nanotubes (MWCNTs) within core-shell fibers prepared in a single step using a modified electrohydrodynamic (EHD) printing technique to promote peripheral nerve regeneration. The structured conduit demonstrated exceptional stability, mechanical properties, and biocompatibility, significantly enhancing the functionality of NGCs. In vitro cell studies revealed that RSC96 cells adhered and proliferated effectively along the oriented fibers, demonstrating a favorable response to the distinctive architectures and properties. Subsequently, a rat sciatic nerve injury model demonstrated effective efficacy in promoting peripheral nerve regeneration and functional recovery. Tissue analysis and functional testing highlighted the significant impact of MWCNT concentration in enhancing peripheral nerve regeneration and confirming well-matured aligned axonal growth, muscle recovery, and higher densities of myelinated axons. These findings demonstrate the potential of oriented lateral architectures with coaxial MWCNT fibers as a promising approach to support long-distance regeneration and encourage directional nerve growth for peripheral nerve repair in clinical applications.

STUDY ON EPOXY RESIN/MULTI-WALLED CARBON NANOTUBES CONDUCTIVE COATING ON AZ31 MAGNESIUM ALLOY AFTER MICRO-ARC OXIDATION

After micro-arc oxidation, the surface properties of AZ31 magnesium alloy have been improved. However, micro-arc oxidation treatment leads to high insulation, which limits its application in electronic devices. To increase conductivity, a conductive coating was developed by adding multi-walled carbon nanotubes (MWCNTs) to the epoxy resin. The microstructure and performance of the coating were tested by SEM, thermogravimetric analyzer, four-probe conductivity meter, high-temperature friction and wear tester, and electrochemical workstation. The results indicate that the optimal conductivity with a resistivity of 303[Formula: see text][Formula: see text]m is obtained when the MWCNT content is at 4[Formula: see text]wt%. In addition, MWCNTs are filled with a network structure of epoxy resin, which increases the density of the coating and enhances their wear and corrosion resistance.

Optimizing nanofluid additives for enhanced thermophysical properties in anionic crude oil for EOR applications

AbstractThis research delved into the effects of introducing multi‐walled carbon nanotubes (MWCNTs) and sodium dodecyl sulphate (SDS) into crude oil with an anionic base, aiming to enhance its thermophysical attributes in the EOR process. The investigation encompassed a range of properties, including interfacial tension, viscosity, density, and electrical conductivity, measured using an LV rheometer with spindle 18. Various ratios of MWCNTs and SDS were mixed with the crude oil to evaluate their impacts. The study uncovered that the 1:1 ratio of MWCNTs to SDS achieved a noteworthy 10% reduction in interfacial tension while minimally affecting viscosity, showing promise for practical applications. Temperature had diverse effects on viscosity and interfacial tension, displaying fluctuating trends. The highest observed result was a substantial 190% viscosity increase at 40°C with a 2:1 ratio, whereas the lowest was a slight −0.81% density change at 60°C for the 1:1 ratio. Additionally, interfacial tension consistently decreased over time for all ratios at various temperatures, with the most significant reductions observed at 40 and 60°C, particularly for the 1:2 and 1:1 ratios. Furthermore, adding MWCNTs and SDS led to a remarkable drop in electrical conductivity, indicating a substantial decrease in salt content within the crude oil. However, it was noted that higher MWCNT concentrations might not be cost‐effective, emphasizing the importance of optimizing additive ratios for a balance between performance and economic viability. This study highlights the potential of tailored nanofluid formulations to improve the thermophysical properties of crude oil, potentially enhancing extraction and refining processes.

Investigation of mechanical and tribological behavior of Al-Ni-Co-MWCNT composites prepared by powder metallurgy technique

The intended research is to improve the mechanical and tribological properties of Al-Ni-Co alloy by reinforcing the alloy with multiwall carbon nanotubes (MWCNT) using powder metallurgy. In this work MWCNT content varied from 0.5, 1.0, and 1.5 as wt. % and mixed with the Al-Ni-Co matrix. The composites are fabricated by cold compaction and conventional sintering technique. The presence of homogenous distribution was analyzed by using scanning electron microscope (SEM) with energy dispersive spectroscopy. The hardness of the composites was also explored by using Vickers' indentation and found that porosity plays a vital role and it directly influences the hardness and the mechanical properties. The wear behavior of the composites was measured using the Pin-on-Disc method at room temperature. The results revealed that 84.5Al-10Ni-4Co-1.5MWCNT possessed less volume loss (0.458 mm3) and coefficient of friction (0.45) compared to other samples. After wear analysis, the surface morphology was analyzed using SEM. The outcome of the research is MWCNT plays a vital role to improve the mechanical and tribological properties of Al-Ni-Co composites.

The effects of Multiwalled Carbon Nanotube to the performance of a refrigeration system

By incorporating nanofluid technology and nanolubricants into compressors, the performance can be enhanced while also lowering worldwide fuel consumption and aiming at developing cleaner, more efficient energy sources and uses. The globe is being confronted with energy security issues and heating, cooling and HVAC systems highly contribute to it. Hence, it is critical to save energy and improve the efficiency of the refrigeration cycle. This study presents experimental and theoretical findings in order to investigate the effect of Polyester (POE)-oil based multiwalled Carbon Nanotube (MWCNT) nanolubricant on the Coefficient of Performance (COP) of a refrigeration system. The objectives of this study is to analyze the stability of MWCNT nanofluids, to obtain the COP of a refrigeration cycle run with pure POE oil and MWCNT nanofluids with different concentrations respectively. The experiment was conducted by preparing 0.55, 0.65 and 0.70 g/l MWCNT nanofluid by using the two step method. The most effective concentration used in the refrigeration system was referred to the one that resulted in the highest COP. It was determined from the experiment that 0.55 g/l MWCNT nanofluid resulted in a higher COP of 5.766 as compared to the other two concentrations. Besides, it showed an improvement of 34.6% in COP as compared to the COP of using pure POE oil in the refrigeration system, which was found to be 4.285. The 0.65 g/l and 0.70 g/l concentration of MWCNT resulted in a COP of 5.618 and 5.617, respectively. The compressor work was also analyzed and was found to be reduced noticeably after adding MWCNT nanoparticles. Hence it can be concluded that the increment of MWCNT concentration in nanofluids increases the COP of the refrigeration system but only up to a certain limit of concentration.

Environmental safety of energy storing devices using carbon nanotubes: possible impacts of waste in aquatic and terrestrial environments

Electric double layer capacitors (EDLC) are energy storage devices based on the charging and discharging electrode-electrolyte interfaces of high surface area materials such as multi-walled carbon nanotubes (MWCNT) and activated carbon (AC). Despite the broad applicability, the final destination of these components is the environment, mainly water and soil, where they can represent impacts on organisms along different trophic levels. Bioassays with Raphidoceles subcapitata, are widely used to evaluate aquatic totoxicity and oligochaetes are good terrestrial bioindicators. The study aimed to evaluate aquatic and terrestrial toxicity of MWCNT from EDLC-type capacitors using bioindicators, R. subcapitata and Eisenia andrei. The MWCNT material was synthesized by the floating catalyst-based chemical vapor deposition method (FC-CVD) on stainless steel (AISI 304L). The MWCNT concentrations for the assays were 0.1 1.0, 10 and 100 mg.L–1 for the bioindicator R. subcapitata and the concentrations of 1, 10 and 100 mg.Kg–1 for bioindicator E. andrei. MWCNT inhibited the algal biomass in a concentration dependent manner at concentrations higher than 10 mg.L–1. In the soil the presence of MWCNT, at the concentrations tested did not cause mortality in the earthworm, but resulted in a significant mass reduction in the exposed organisms after 14 days. In the cytology analysis, it was not observed the production of micronuclei, but cytoplasmic vacuolization and nuclear atypia in coelomocytes were frequent. In the comet assay, there was a predominance of nucleoids in the stage 1 classification. Thus, no genotoxic effect was demonstrated in these organisms. The concentrations that showed toxic effects are within the range of environmentally expected concentrations. MWCNT are released from EDLC and may pose an occupational and environmental risk.

The synergistic impact of multi walled carbon nanotubes on microstructural, morphological, and optical properties of polyaniline films

AbstractNanocomposite of polyaniline (PANI) and multi walled carbon nanotube (MWCNT) was synthesised by ex‐situ solution mixing process in the N‐Methyl‐2‐Pyrrolidinone (NMP) solvent medium by varying the concentration of MWCNT in the PANI matrix. PANI‐MWCNT composite films were prepared by the drop casting method. The morphology, structure and chemical composition of PANI and PANI‐MWCNT nanocomposites were characterised by scanning electron microscopy (SEM), transmission electron microscopy (TEM), x‐ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT‐IR) spectra. The experimental findings suggested a favourable synergy between PANI and MWCNTs. PANI‐MWCNT nanocomposite formed as randomly oriented nanofibrous clusters was confirmed, and the bandgap of the composites was found to be gradually decreased with the increase in concentration of MWCNT in the PANI matrix. The calculation of crystallinity index, crystallite size, average d‐spacing, dislocation density, lattice strain, and inter chain separation of the samples were conducted by XRD analysis. When the MWCNT concentration increased from 0.05 % w/v to 0.5 % w/v, a rise in the degree of crystallinity from 3.39 % to 52.46 %, dislocation density from 0.03315×10−3(nm−2)to 0.07133×10−3 (nm−2) and lattice strain from 8.6821×10−3 to 12.9843×10−3, accompanied by a reduction in both crystallite size and inter‐chain separation were observed .The microcrystalline behaviour and crystalline orientation of the PANI‐MWCNT composites were correlated with the bandgap studies. The composite formation improved the thermal stability of PANI. The co‐relation between the crystallinity parameters and fine tuning of optical bandgap and the control over the defect levels were done in this study. This synergy suggests that these composites are suitable candidates for linear and nonlinear optical (NLO) applications.

BIOCOMPATIBLE ELASTIC POLYMER NANOCOMPOSITES BASED ON MULTIWALLED CARBON NANOTUBES FOR APPLICATION IN CARDIOVASCULAR SURGERY

HighlightsThe incorporation of multi-walled carbon nanotubes into the structure of the poly(styrene-block-isobutylene-block-styrene) polymer matrix leads to an increase in the tensile strength and Young's modulus of the nanocomposites. The resulting nanocomposites retain high biocompatibility and can be used as elements of implanted cardiovascular products. AbstractAim. To synthesize and modify poly(styrene-block-isobutylene-block-styrene) (SIBS) with two types of multi-walled carbon nanotubes (MWCNTs) in different concentrations to improve its mechanical properties.Methods. SIBS was synthesized by controlled cationic polymerization. Polymer nanocomposites were prepared using ultrasonic dispersion followed by casting films from a polymer solution. The resulting nanocomposite films were subjected to mechanical tests under uniaxial tensile conditions. Tensile strength, elastic-strain properties, and plastic deformation under cyclic loading were assessed. The structure of the nanocomposites was analyzed by scanning electron microscopy. The hydrophilicity of the surface of the materials was studied by measuring the contact angle with water. The cytotoxicity of the resulting polymer films was assessed by the viability and metabolic activity of endothelial cells cultured on the surface of the nanocomposites.Results. Polymer nanocomposites with a uniform distribution of MWCNTs in the polymer matrix were obtained. SIBS films modified with 1% MWCNTs with a diameter of 50–90 nm showed an increase in tensile strength by 16.4% compared to SIBS polymer. Increasing the concentration of MWCNTs to 8% led to a decrease in the strength of polymer materials by 19,6%. The inclusion of nanoparticles into the polymer matrix significantly increased the Young's modulus of the studied polymers with a MWCNT content above 4%. With an increase in the content of MWCNTs in the nanocomposites, an increase in hydrophilicity was also observed, while the cytotoxicity of the samples towards endothelial cells was not noted.Conclusion. Nanocomposites based on SIBS and MWCNTs, due to their high strength and biocompatibility, can become a promising material for the development of various medical products, in particular prosthetic heart valves.

Study of the Effect of Multi-Walled Carbon Nanotubes on the Mechanical Properties of Poly(Vinyl Alcohol)/Polyaniline Blend Film

In this research, poly(vinyl alcohol)/polyaniline blend films were fabricated using solution casting technique with different weight ratios of PANI (2, 4, 6, 8, and 10) wt.%. The results showed that the best ratio of the polymer blend was (92% PVA/8% PANI), based on the electrical conductivity of direct current. The results showed that 8 wt.% PANI possessed the highest conductivity. Then, the composite films were prepared by adding multi-walled carbon nanotubes (MWCNT) to the optimum ratio of the polymer blend as a base material and at different weight ratios (0, 1, 3, 5, 7 wt.%). A tension device was used to examine and characterize the prepared samples. It was found that the addition of MWCNT to PVA/PANI caused an obvious decrease in elongation while there was an increase in tension strength and “Young’s modulus”. Optical microscopy results showed a good picture of the distribution of MWCNT particles for composites up to 1 wt.% MWCNT. But, some aggregations can be observed in films with 3, 5, and 7 wt.% MWCNT content.

Study on the Properties of Multi-Walled Carbon Nanotubes (MWCNTs)/Polypropylene Fiber (PP Fiber) Cement-Based Materials.

In order to improve the mechanical properties and durability of cement-based materials, a certain amount of multi-walled carbon nanotubes (MWCNTs) and polypropylene fiber (PP fiber) were incorporated into cement-based materials. The mechanical properties of the multi-walled carbon nanotubes/polypropylene fiber cement-based materials were evaluated using flexural strength tests, compressive strength tests, and splitting tensile tests. The effects of multi-walled carbon nanotubes and polypropylene fiber on the durability of cement-based materials were studied using drying shrinkage tests and freeze-thaw cycle tests. The effects of the multi-walled carbon nanotubes and polypropylene fibers on the microstructure and pore structure of the cement-based materials were compared and analyzed using scanning electron microscopy and mercury intrusion tests. The results showed that the mechanical properties and durability of cement-based materials can be significantly improved when the content of multi-walled carbon nanotubes is 0.1-0.15%. The compressive strength can be increased by 9.5% and the mass loss rate is reduced by 27.9%. Polypropylene fiber has little effect on the compressive strength of the cement-based materials, but it significantly enhances the toughness of the cement-based materials. When its content is 0.2-0.3%, it has the best effect on improving the mechanical properties and durability of the cement-based materials. The flexural strength is increased by 19.1%, and the dry shrinkage rate and water loss rate are reduced by 14.3% and 16.1%, respectively. The three-dimensional network structure formed by the polypropylene fiber in the composite material plays a role in toughening and cracking resistance, but it has a certain negative impact on the pore structure of the composite material. The incorporation of multi-walled carbon nanotubes can improve the bonding performance of the polypropylene fiber and cement matrix, make up for the internal defects caused by the polypropylene fiber, and reduce the number of harmful holes and multiple harmful holes so that the cement-based composite material not only has a significant increase in toughness but also has a denser internal structure.

Experimental and numerical investigation on the cold harvest of composite phase change materials for building energy conservation

This paper investigates the cold energy storage of a horizontal shell-tube latent heat thermal energy storage (LHTES) unit for the cold harvest during night time. An experimental apparatus containing a horizontal circular tube with circumferential heating/cooling was designed and developed. Paraffin based phase change material (PCM) with a melting temperature of 27 °C was adopted as the cold harvest media. To improve the heat transfer rate, multi-walled carbon nanotubes (MWCNTs) were mixed with the paraffin to form a composite PCM with high thermal conductivity. A corresponding model of the composite PCM was developed and verified against the experimental data. Numerical simulations were performed for different boundary temperatures and concentrations of MWCNTs. The results show that when the heat transfer temperature difference is 20 °C, 0.05 wt% nanoparticles increase the melting rate of PCMs. When the heat transfer temperature difference was 40 °C, 0.10 wt% nanoparticles significantly affect the PCM melting rate. For low or high temperature (heat transfer temperature difference of 10 °C and 80 °C), the addition of nanoparticles is not conducive to improving the melting rate.

Self-sensing characteristics of smart high-performance cementitious composites containing multiwall carbon nanotubes, steel fibers, and steel slag aggregates under compression

Smart high-performance cementitious composite (SHPCC) with sensing abilities, high mechanical, and high durability is a potential smart material instead of current sensors applied for structural health monitoring systems of infrastructures. This study deeply investigated the sensing properties of SHPCCs containing multiwall carbon nanotubes (MWCNTs), steel fibers, and steel slag aggregates (SSAs) under compression. SHPCCs containing different contents of MWCNTs (0.1% and 0.5% of cement weight), steel fibers (2 and 4 vol%), SSAs (10% and 50% instead of sand), and free water (fully dried and moisture specimens) were prepared and evaluated. The results indicated that the SSA content was a key factor controlling the electrically conductive network response and the stress-sensing ability of SHPCCs. MWCNTs significantly enhanced the stress-sensing ability of fully dried SHPCCs under compression. Besides, the free water content in pore systems significantly influenced the stress-sensing ability of SHPCCs. A conductive network of SHPCCs with MWCNTs, fibers, SSAs, and free water at micro and nano levels was proposed and analyzed to explain the electrical resistivity response under compression.

A novel bio-based composite phase change material with excellent photo-thermal conversion capability for solar energy harvesting and energy storage

Organic solid-liquid phase change materials (PCMs) have been widely studied in the field of photo-thermal conversion and thermal energy storage. However, problems such as easy leakage and low efficiency of photo-thermal conversion limit their applications. To solve these problems, this study developed a shape-stable composite phase change material (CPCM) using sponge tissue of discarded corn stem (STCS), polyethylene glycol (PEG), pyrrole (Py), and multi-walled carbon nanotube (MWCNT). PPy and MWCNT enable the CPCM to have excellent photo-thermal conversion capability and thermal conductivity. With 0.2 % MWCNT content, the CPCM achieved a thermal conductivity of 0.4609 W/m·K and a photo-thermal conversion efficiency exceeding 95.3 %. It also demonstrated high enthalpy and relative enthalpy efficiency (152.2 J/g, 96.01 %). Moreover, the CPCM exhibited remarkable shape and thermal stability, with no pyrolysis below 340 °C and nearly unchanged enthalpy after 100 cycles. Meanwhile, this CPCM also showed excellent ability in promoting seawater desalination. This work provides a new idea for recycling of agricultural waste and storage of solar energy as well as desalination of seawater.

Mechanical and piezoresistive properties of multi-walled carbon nanotubes reinforced epoxy matrix composites for pipeline monitoring

Pipeline deformation monitoring is of vital importance for pipeline maintenance. However, no durable and effective methods have been seen for deformation monitoring of buried pipes, especially drainage pipes. In this paper, an embedded multi-walled carbon nanotubes (MWCNTs) reinforced epoxy (EP) matrix composite for pipeline monitoring was developed. The bending properties, piezoresistive properties and stability of MWCNTs/EP composites were investigated using three-point bending tests, cyclic tests, resistivity tests, and scanning electron microscope (SEM) observations. The results indicated that when the MWCNTs content was at 0.1 wt%, the bending strength, bending modulus and bending strain increased by 12.3 %, 8.7 % and 25.1 % respectively. The conductive percolation threshold was at 0.7 wt%, and the resistance changed in three stages under bending. In addition, the MWCNTs/EP composites had stable piezoresistive properties under different loading rates and small strain cyclic (ε < 1.5 %). The MWCNTs content and dispersion effect were the main factors affecting the bending properties of MWCNTs/EP composites, while the resistance change mainly originated from the change of the MWCNTs conductive network. This work provided a new idea for pipeline deformation monitoring.

A comparative study on the influence of MWCNT, GO, and Al(OH)3 gel matrix modification on hierarchical structured composite reinforced with needle-punched jute fiber and glass fiber

The main objective of this paper was to identify the influence of different filler materials on the properties of hybrid composites. The hybrid composites were fabricated using randomly oriented glass fiber mats, needle-punched jute fiber mats, and epoxy resin as the matrix material. Three different kinds of filler materials were studied: Multi-Walled Carbon Nanotubes (MWCNTs), Graphene Oxide (GO), and Aluminum Hydroxide (AlOH) nanoparticles. The secondary reinforcements were dispersed in the epoxy matrix through ultrasonication. The composites were made by conventional hand lay-up followed by applying high pressure and temperature under a hydraulic press to effectively cure and minimize voids within the final composite. These were compared with the properties of the unmodified composite containing no filler. The influence on mechanical properties was evaluated through tensile, flexural, and impact tests. Failure modes of the fractured tensile specimen were observed through Scanning Electron Microscopy (SEM). Fourier Transform Infrared (FTIR) analysis was done to observe the changes in the chemical structure upon the addition of secondary reinforcements. Lastly, water absorption behavior and flame retardancy were observed as well. The results showed that MWCNT resulted in the composite exhibiting superior properties and GO, on the contrary, led to the deterioration of the properties. This could be because an optimum concentration of MWCNT was used, whereas this was not the case for GO filler. The addition of MWCNT resulted in a more substantial but brittle composite, while AlOH enhanced the ductility of the composite by compromising the overall strength. Hence, it can be concluded that MWCNT resulted in the formation of composites with the most desired properties.

Tailoring Optoelectronic Properties of ZnO Nanoparticles via Incorporation of Multiwalled Carbon Nanotube Contents on of ZnO/MWCNT Nanocomposites

The present study demonstrates the tailoring of optoelectronic properties of ZnO nanoparticles (NPs) by adding multi-walled carbon nanotubes (MWCNTs) at different weight ratios. ZnO/MWCNT nanocomposites were successfully prepared using the solution blending method, and the optical spectra of all samples were determined using a UV–vis spectrometer. An increase in the optical absorption coefficient (α) and extinction coefficient (k) was observed with an increase in MWCNT content, resulting in the significant ability to attenuate incident light in ZnO/MWCNT nanocomposites compared to pure ZnO NPs. The optical band gap of pure ZnO NPs decreased from 3.26 eV to 2.58 eV in the ZnO/50 wt% MWCNT nanocomposite. The refractive index values ranged from 1.66 to 1.61 as the wavelength varied between 400 nm and 700 nm. Furthermore, the incorporation of MWCNTs in the ZnO/MWCNT nanocomposite had an impact on various dispersion parameters related to the refractive index. With increasing MWCNT content, the dielectric constant (ε 0) decreased from 2.40 to 1.96, while the mean oscillator wavelength (λ 0) increased from 157.7 nm to 164.2 nm and the oscillator strength (S0) decreased from 5.93 × 10−5 nm−2 to 3.70 × 10−6 nm−2. The localized density of state (N/m*) increased from 7.45 × 1057 to 20.8 × 1057 (m3 Kg) −1, and the long wavelength refractive index (ε ∞) rose from 3.683 to 4.745. Moreover, the plasma frequency (ω p) of the electron exhibited an increase from 2.15 × 1031 to 6.01 × 1031 Hz. These findings highlight the potential of tailoring the optoelectronic properties of ZnO NPs through the incorporation of MWCNTs, paving the way for the development of novel materials with improved optoelectronic characteristics for a wide range of applications.

The Influence of Carbon Nanotubes on the Physical and Chemical Properties of Nanocomposites Based on Unsaturated Polyester Resin

The new actual scientific direction is in the development of different nanocomposites and the study of their medical–biological, physicochemical, and physicomechanical properties. One way to expand the functionality of nanocomposites and nanomaterials is to introduce carbon nanostructures into the polymer matrix. This study presents the properties of unsaturated polyester resins (Estromal, LERG S.A.) based on PET recyclate with multi-walled carbon nanotubes (MWCNTs): their mechanical and thermomechanical characteristics, resistance to ultraviolet radiation (UV-vis), and chemical resistance properties. The properties of the obtained materials were characterized using physical–chemical research methods. The changes in the properties of the composites for MWCNT content of 0.1, 0.3, and 0.5 wt % were determined. The results showed positive influences on the thermomechanical and mechanical properties of nanocomposites without significant deterioration of their gloss. Too much CNT added to the resin leads to heterogeneity of the composite structure.

Effects of multi‐walled carbon nanotubes on structures and properties of heat‐resistant poly(m‐phenylene isophthalamide)‐based hollow fiber ultrafiltration membranes

AbstractThis study is the first attempt to fabricate a heat‐resistant hollow fiber ultrafiltration membrane using poly(m‐phenylene isophthalamide) (PMIA) polymer material, which has rarely been used as conventional polymeric membrane materials. Multi‐walled carbon nanotubes (MWCNTs) are incorporated as reinforcing agents. The PMIA polymer synthesized for this study exhibited an inherent viscosity of 1.6 dL/g, confirming its suitability for membrane fabrication, and successful synthesis was verified through Fourier‐transform infrared analysis. To enhance the dispersibility of MWCNTs during dope solution preparation and their interaction with the PMIA matrix, MWCNTs were acid‐treated and surface characteristics of the acid‐treated MWCNTs were confirmed through x‐ray photoelectron spectroscopy analysis. Scanning electron microscope analysis revealed that the introduction of MWCNTs resulted in thicker PMIA hollow fiber ultrafiltration membranes with symmetrical finger‐like and sponge‐like pore structures. Interestingly, unlike the typical polymer composite systems containing MWCNTs, which often show a dependence on MWCNT content, the mechanical properties of the PMIA/MWCNT membranes in this study seem to exhibit high variability and are not contingent on the MWCNT content. Additionally, filtration performance studies demonstrated that the introduction of MWCNTs substantially increased water permeability, particularly at 1.0 wt% MWCNT content, resulting in a remarkable 130% enhancement compared to pristine PMIA membrane. Simultaneously, even with a small quantity of MWCNTs, the rejection performance of the PMIA/MWCNT membrane witnessed significant improvement due to the reduction in average pore size, effectively overcoming the commonly observed trade‐off phenomenon. In summary, this study clearly showed the effects and changes on the structure and properties of a heat‐resistant PMIA‐based hollow fiber ultrafiltration membranes due to the introduction of MWCNTs.Highlights Heat‐resistant poly(m‐phenylene isophthalamide)‐based hollow fiber ultrafiltration membranes Introduction of multi‐walled carbon nanotubes (MWCNTs) into PMIA membrane as a reinforcing agent Unique structural changes of PMIA membrane originated from the MWCNTs Enhanced tensile strength of PMIA/MWCNT membranes Simultaneous improvement of filtration performance due to MWCNTs