Calcium-enriched Mixture Cement Research Articles

Effect of calcium chloride on physical properties of calcium‐enriched mixture cement

The aim of this study was to evaluate the effect of adding 10% calcium chloride (CaCl2) on the setting time, solubility and the pH of calcium-enriched mixture (CEM) cement. Setting time was assessed in accordance with American Dental Association specification N°57. Solubility was measured at 24 and 72 h, 7 and 14 days in hydrated and dehydrated conditions by calculating weight change. The pH of MiliQ water in which the CEM cement samples were immersed was measured immediately after each time interval with and without the addition of CaCl2. The data were analysed using the Mann-Whitney U-test and the Student's t-test. The initial setting time was significantly decreased after the addition of 10% CaCl2. The pH of water increased immediately when in contact with the cements in both groups. The weight loss of hydrated and dehydrated specimens was more than 3% and was significantly reduced by the addition of 10% CaCl2.

Effects of Chlorhexidine and Sodium Hypochlorite on the Setting Time of Calcium-Enriched Mixture Cement.

Introduction:The aim of the present study was to evaluate whether adding 2% chlorhexidine (CHX) and 2.6% sodium hypochlorite (NaOCl) to calcium-enriched mixture (CEM) cement would affect its setting time (ST), or not. Methods and Materials: In this study, the setting time of CEM cement was evaluated in three groups (n=9) as follows: group 1; CEM cement, group 2; CEM cement+2% CHX and group 3; CEM cement+2.6% NaOCl. Then the mean values of ST were calculated and the Kolmogorov-Smirnov test was used to evaluate the normal distribution of data. The Kruskal-Wallis and Mann-Whitney U tests were used for statistical analysis. Statistical significance was set at 0.05.Results:The mean ST for groups 1, 2 and 3 were 105, 120 and 220 min, respectively. There was a significant increase in the duration of ST in group 3 (NaOCl) in comparison with the two other groups (P<0.05). Conclusion:NaOCl significantly increased the ST of CEM cement, whereas chlorhexidine did not alter the ST.

Evaluation of the Clinical and Radiographic Outcomes of Pulpotomy in Primary Molars using Formocresol, CEM Cement and Sodium Hypochlorite 5%

<b>Aim:</b> This in vitro study was carried out to assess the clinical and radiographic success of pulpotomy in primary molars following the use of formocresol, sodium hypochlorite 5% (NaCOl) and Calcium Enriched Mixture (CEM) cement. <b>Materials and methods:</b> This study was conducted on 108 primary molars of 5-8 year old children who referred to the pediatric dentistry, Isfahan faculty of dentistry. The selected teeth were equally distributed and randomly assigned to 3 groups of formocresol, sodium hypochlorite and CEM cement. After taking the initial radiography, standard pulpotomy was carried out by using formocresol, CEM cement and sodium hypochlorite 5%, and the teeth were restored by Stainless Steel Crown (SSC). The clinical and radiographic evaluations were performed at 6 and 12-month follow-ups. Data was analyzed by chi-square and Relative Risk statistical tests. <b>Results:</b> After 6 months, all (100%) of the pulpotomy medicaments were clinically successful. Also, there was no clinically significant difference between the results of primary molar pulpotomy in these 3 groups in the 1-year follow-up (p=0.129). There was not any significant difference between three groups in the first follow-up (p=0.364) and second follow-up (p=0.100). Conclusion: There was no significant difference among the success rates of the pulpotomy medicaments used in primary molars. Moreover, the clinical and radiographic success rates of NaOCl 5% and CEM cement were comparable to those of formocresol.

In Vitro Spectrophotometry of Tooth Discoloration Induced by Tooth-Colored Mineral Trioxide Aggregate and Calcium-Enriched Mixture Cement.

Introduction: There are numerous factors that can lead to tooth discoloration after endodontic treatment, such as penetration of endodontic materials into the dentinal tubules during root canal treatment. The aim of this in vitro study was to compare discoloration induced by tooth colored mineral trioxide aggregate (MTA) and calcium-enriched mixture (CEM) cement in extracted human teeth. Methods and Materials:Thirty two dentin-enamel cuboid blocks (7×7×2 mm) were prepared from extracted maxillary central incisors. Standardized cavities were prepared in the middle of each cube, leaving 1 mm of enamel and dentin on the labial surface. The specimens were randomly divided into two study groups (n=12) and two positive and negative control groups (n=4). In either study groups the cavities were filled with MTA or CEM cement. The positive and negative control groups were filled with blood or left empty, respectively. The cavities were sealed with composite resin and stored in normal saline. Color measurement was carried out by spectrophotometry at different time intervals including before (T0), and 1 week (T1), 1 month (T2) and 6 months (T3) after placement of materials. Repeated-measures ANOVA was used to compare the discoloration between the groups; the material type was considered as the inter-subject factor. The level of significance was set at 0.05. Results:No significant differences were detected between the groups in all time intervals (P>0.05). Conclusion:Tooth discoloration was similarly detectable with both of the two experimental materials.

The Effect of Different Mixing Methods on Working Time, Setting Time, Dimensional Changes and Film Thickness of Mineral Trioxide Aggregate and Calcium-Enriched Mixture.

Introduction:The aim of the present study was to evaluate the effect of different mixing techniques (conventional, amalgamator and ultrasonic mixing) on the physical properties the working time (WT), setting time (ST), dimensional changes (DC) and film thickness (FT)] of calcium-enriched mixture (CEM) cement and mineral trioxide aggregate (MTA). Methods and Materials:The mentioned physical properties were determined using the ISO 6786:2001 specification. Six samples of each material were prepared for three mixing techniques (totally 36 samples). Data were analyzed using descriptive statistics, two-way ANOVA and Post Hoc Tukey’s tests. The level of significance was defined at 0.05. Results: Irrespective of mixing technique, there was no significant difference between the WT and FT of the tested materials. Except for the DC of MTA and the FT of the all materials, other properties were significantly affected with mixing techniques (P<0.05). The ultrasonic technique decreased the ST of MTA and CEM cement and increased the WT of CEM cement (P<0.05). Conclusion:The mixing technique of the materials had no significant effect on the dimensional changes of MTA and the film thickness of both materials.

Coronal microleakage of three different dental biomaterials as intra-orifice barrier during nonvital bleaching.

This study was designed to assess the microleakage of glass-ionomer (GI), mineral trioxide aggregate (MTA), and calcium-enriched mixture (CEM) cement as coronal orifice barrier during walking bleaching. In this experimental study, endodontic treatment was done for 70 extracted human incisors without canal calcification, caries, restoration, resorption, or cracks. The teeth were then divided into three experimental using "Simple randomization allocation" (n = 20) and two control groups (n = 5). The three cements were applied as 3-mm intra-orifice barrier in test groups, and bleaching process was then conducted using a mixture of sodium perborate powder and distilled water, for 9 days. For leakage evaluation, bovine serum albumin marker was traced in a dual-chamber technique with Bradford indicator. The Kruskal-Wallis and Mann-Whitney tests were used for statistical analysis. The mean ± standard deviation leakage of samples from negative control, positive control, GI, MTA, and CEM cement groups were 0.0, 8.9 ± 0.03, 0.47 ± 0.02, 0.48 ± 0.02, and 0.49 ± 0.02 mg/mL, respectively. Statistical analysis showed no significant difference between three experimental groups (P > 0.05). It is concluded that GI, MTA, and CEM cements are considered as suitable intra-orifice barrier to provide coronal seal during walking bleaching.

The Effect of Thickness on the Sealing Ability of CEM Cement as a Root-end Filling Material.

Background and aims. Different materials have been used for root-end filling during surgical endodontic treatment. The aim of this in vitro study was to evaluate the dye penetration in different thicknesses of calcium enriched mixture (CEM) cement as root-end filling material. Materials and methods. Following root canal filling in 70 extracted human single-rooted premolar teeth, the apical 3 mm of their root-ends was resected; the root-end cavities with depths of 1, 2 and 3 mm were prepared by ultrasonic retrotips and filled with CEM cement. After setting of cement, the roots were immersed in 2% Rhodamine B and the dye leakage was measured under stereomicroscope (×16) using Image J software. The data were analyzed by one-way ANOVA and Bonferroni post hoc tests at 5% significance level. Results. The means and standard deviations of dye penetration in the 1, 2, and 3 mm groups were 3395.5±1893.4, 3410.4±1440.5, and 2581.6±1852.9 μm, respectively. The one-way ANOVA analysis indicated significant differences (P < 0.001); however, the Bonferroni post hoc test revealed that only the positive control group differed significantly from the experimental groups (P < 0.001). Conclusion. The findings demonstrated CEM cement to have an adequate root-end sealing ability in 3-mm thickness.

Role of calcium-enriched mixture in endodontics

Calcium-enriched mixture (CEM) has been recently introduced as a hydrophilic tooth-colored cement. The CEM cement powder is composed of calcium oxide, calcium sulfate, phosphorus oxide, and silica as major elements. CEM is alkaline cement (pH~11) that releases calcium hydroxide (CH) during and after setting. The physical properties of CEM, such as flow, film thickness, and primary setting time are favorable. This cement is biocompatible and induces formation of cementum, dentin, bone and periodontal tissues. This novel cement has an antibacterial effect comparable to CH and superior to mineral trioxide aggregate (MTA) and sealing ability similar to MTA. Its clinical applications include pulp capping, pulpotomy, root-end filling and perforation repair. This review describes the composition, properties and clinical applications of CEM in endodontics.

The effect of different mixing methods on the flow rate and compressive strength of mineral trioxide aggregate and calcium-enriched mixture.

Flow rate (FR) and compressive strength (CS) are important properties of endodontic biomaterials that may be affected by various mixing methods. The aim of this experimental study was to evaluate the effect of different mixing methods on these properties of mineral trioxide aggregate (MTA) and calcium-enriched mixture (CEM) cement. Hand, amalgamator and ultrasonic techniques were used to mix both biomaterials. Then 0.5 mL of each mixture was placed on a glass slab to measure FR. The second glass slab (100 g) was placed on the samples and 180 sec after the initiation of mixing a 100-g force was applied on it for 10 min. After 10 min, the load was removed, and the minimum and maximum diameters of the sample disks were measured. To measure the CS, 6 sample of each group were placed in steel molds and were then stored in distilled water for 21 h and 21 days. Afterwards, the CS test was performed. Data were analyzed with multi-variant ANOVA and post hoc Tukey tests. The level of significance was set at 0.05. There were significant differences in FR of MTA and CEM cement with different mixing techniques (P<0.05). In the MTA group, none of the mixing techniques exhibited a significant effect on CS (P>0.05); however, in CEM group the CS at 21-h and 21-day intervals was higher with the hand technique (P<0.05). Mixing methods affected the flowability of both biomaterials and compressive strength of CEM cement.

Effect of Different pH Values on the Compressive Strength of Calcium-Enriched Mixture Cement.

The aim of this study was to evaluate the compressive strength of calcium-enriched mixture (CEM) cement in contact with acidic, neutral and alkaline pH values. The cement was mixed according to the manufacturer's instructions, it was then condensed into fourteen split molds with five 4×6 mm holes. The specimens were randomly divided into 7 groups (n=10) and were then exposed to environments with pH values of 4.4, 5.4, 6.4, 7.4, 8.4, 9.4 and 10.4 in an incubator at 37(°) C for 4 days. After removing the samples from the molds, cement pellets were compressed in a universal testing machine. The exact forces required for breaking of the samples were recorded. The data were analyzed with the Kruskal-Wallis and Dunn tests for individual and pairwise comparisons, respectively. The level of significance was set at 0.05. The greatest (48.59±10.36) and the lowest (9.67±3.16) mean compressive strength values were observed after exposure to pH value of 9.4 and 7.4, respectively. Alkaline environment significantly increased the compressive strength of CEM cement compared to the control group. There was no significant difference between the pH values of 9.4 and 10.4 but significant differences were found between pH values of 9.4, 8.4 and 7.4. The acidic environment showed better results than the neutral environment, although the difference was not significant for the pH value of 6.4. Alkaline pH also showed significantly better results than acidic and neutral pH. The compressive strength of CEM cement improved in the presence of acidic and alkaline environments but alkaline environment showed the best results.

The effect of chlorhexidine on the push-out bond strength of calcium-enriched mixture cement.

The aim of this in vitro study was to evaluate the effect of 2% chlorhexidine (CHX) on the push-out bond strength (BS) of calcium-enriched mixture (CEM) cement. Root-dentin slices from 60 single-rooted human teeth with the lumen diameter of 1.3 mm were used. The samples were randomly divided into 4 groups (n=15), and their lumens were filled with CEM cement mixed with either its specific provided liquid (groups 1 and 3) or 2% CHX (groups 2 and 4). The specimens were incubated at 37(°)C for 3 days (groups 1 and 2) and 21 days (groups 3 and 4). The push-out BS were measured using a universal testing machine. The slices were examined under a light microscope at 40× magnification to determine the nature of bond failure. The data were analyzed using the two-way ANOVA. For subgroup analysis the student t-test was applied. The level of significance was set at 0.05. After three days, there was no significant difference between groups 1 and 2 (P=0.892). In the 21-day specimens the BS in group 3 (CEM) was significantly greater than group 4 (CEM+CHX) (P=0.009). There was no significant difference in BS between 3 and 21-day samples in groups 2 and 4 (CEM+CHX) (P=0.44). However, the mean BS after 21 days was significantly greater compared to 3-day samples in groups 1 and 3 (P=0.015). The bond failure in all groups was predominantly of cohesive type. Mixing of CEM with 2% CHX had an adverse effect the bond strength of this cement.

Current perspectives of bio-ceramic technology in endodontics: calcium enriched mixture cement - review of its composition, properties and applications.

Advancements in bio-ceramic technology has revolutionised endodontic material science by enhancing the treatment outcome for patients. This class of dental materials conciliates excellent biocompatibility with high osseoconductivity that render them ideal for endodontic care. Few recently introduced bio-ceramic materials have shown considerable clinical success over their early generations in terms of good handling characteristics. Calcium enriched mixture (CEM) cement, Endosequence sealer, and root repair materials, Biodentine and BioAggregate are the new classes of bio-ceramic materials. The aim of this literature review is to present investigations regarding properties and applications of CEM cement in endodontics. A review of the existing literature was performed by using electronic and hand searching methods for CEM cement from January 2006 to December 2013. CEM cement has a different chemical composition from that of mineral trioxide aggregate (MTA) but has similar clinical applications. It combines the biocompatibility of MTA with more efficient characteristics, such as significantly shorter setting time, good handling characteristics, no staining of tooth and effective seal against bacterial leakage.

The Effect of Acidic pH on Microleakage of Mineral Trioxide Aggregate and Calcium-Enriched Mixture Apical Plugs.

The purpose of this laboratory study was to evaluate the effect of acidic pH on the sealing ability of calcium-enriched mixture (CEM) cement and mineral trioxide aggregate (MTA) apical plugs. Seventy single-rooted human maxillary anterior teeth were recruited. The teeth were randomly divided into 4 experimental groups (n=15), and 1 negative and 1 positive control groups of 5. The root canals were cleaned and shaped and the terminal 3 mm of the roots were resected. Then MTA and CEM cement plugs were condensed in apical region with 3 mm thicknesses. The samples were exposed to pH values of 5.5 and 7.4. Leakage was evaluated by the fluid filtration technique at 1, 7, 14, 30 day intervals. Data were analyzed by the repeated measures MANOVA, one-way ANOVA and MANOVA/Bonferroni test. Acidic pH significantly reduced the sealing ability of MTA after 1, 14 and 30 days (P<0.05). The rate of microleakage in CEM cement samples in acidic pH was significantly greater than that in neutral pH in day 30 (P<0.05). There was no significant difference between the sealing property of MTA and CEM cement at both pH levels (P>0.05). It can be concluded that the CEM cement exhibited similar sealing ability as MTA at both pH levels. In addition, an acidic pH environment reduced the sealing ability of MTA and CEM cement after 30 days.

Effect of acidic environment on the push-out bond strength of calcium-enriched mixture cement.

This laboratory study was performed to evaluate the effect of different acidic pH values on the push-out bond strength of calcium-enriched mixture (CEM) cement. Forty-eight root dentin slices were obtained from freshly extracted single rooted human teeth and their lumen were instrumented to achieve a diameter of 1.3 mm. Then, CEM cement was mixed according to manufacturers' instruction and placed in the lumens with minimal pressure. The specimens were randomly divided into four groups (n=12) which were wrapped in pieces of gauze soaked in either synthetic tissue fluid (STF) (pH=7.4) or butyric acid which was buffered at pH values of 4.4, 5.4 and 6.4. They were then incubated for 4 days at 37°C. The push-out test was performed by means of the universal testing machine. Specimens were then examined under a digital light microscope at 20× magnification to determine the nature of the bond failure. The data were analyzed using the Kruskal-Wallis test followed by Dunn's test for pairwise comparisons. The highest push-out bond strength (10.19±4.39) was seen in the pH level of 6.4, which was significantly different from the other groups (P<0.05). The values decreased to 2.42±2.25 MPa after exposure to pH value of 4.4. Lower pH value of highly acidic environments (pH=4.4), adversely affects the force needed for displacement of CEM cement; while in higher pH values (pH=6.4) the bond-strength was not affected. CEM cement is recommended in clinical situations where exposure to acidic environment is unavoidable.

Sealing ability of mineral trioxide aggregate and calcium-enriched mixture cement as apical barriers with different obturation techniques.

Endodontic treatment in pulpless immature teeth is challenging due to the lack of an apical stop. Insertion of an apical plug is an alternative to conventional long-term apexification with calcium hydroxide. The aim of this study was to compare the apical microleakage of mineral trioxide aggregate (MTA) and calcium-enriched mixture (CEM) cement as apical plugs with three different obturation techniques. This experimental study was conducted on 130 single rooted human teeth with one canal. Samples were randomly divided into 2 experimental groups (n=60) and two negative and positive control groups containing 5 samples each. After cleaning and shaping, an open apex configuration was prepared in all samples. MTA or CEM cement apical plugs with 5 mm thicknesses were placed. Then, each group was divided to 4 subgroups and the remaining space of root canals were filled with either lateral compaction or thermoplasticized injectable gutta-percha or was obturated by filling the entire canal with apical plug material. In one remaining subgroup the canal space was left unfilled. Microleakage was measured by the fluid filtration method and results were analyzed by means of the two-way ANOVA test. There were no significant differences between microleakage of MTA and CEM cement apical plugs (P=0.92). The difference between three obturation methods was not significant, either (P=0.39). MTA and CEM cement have similar sealing ability as apical plugs and no significant difference was found in microleakage of the three groups.

Cytotoxic effects of various mineral trioxide aggregate formulations, calcium-enriched mixture and a new cement on human pulp stem cells.

This in vitro study compared the cytotoxic effects of three commercially available MTA formulations naming ProRoot MTA (PMTA), Angelus MTA (AMTA), and Root MTA (RMTA), with calcium-enriched mixture (CEM) cement and a new nanohybrid MTA (NMTA) on human dental pulp stem cells (DPSC). Four disc-shaped specimens of each material were prepared. After completion of setting, 2 different (neat and 1/2) elutes of the test materials were made. Then in each cavity of a 96-well plate, 3000 cells were seeded and incubated in a humidified incubator with 5% CO2 and 95% air at 37(°)C for 24 h. After this period, the culture medium of each well was replaced with 200 μL of test material elutes. Plain culture medium was used as the negative control and distilled water as the positive control group. Cell viability was assessed using 2, 5-diphenyl-SH-tetrazelium bromide colorimetric assay, aka Mosmann's tetrazolium toxicity (MTT) assay, at three time intervals (24, 48, and 72 h after mixing). Data were analyzed using the ANOVA and Tukey's post hoc test (P=0.05). After 24 h, the viability of cells in neat concentration had no significant differences (P>0.05) except for the NMTA. However, CEM and AMTA, at 1/2 concentration exerted significant proliferative effects on cells. At 48 and 72-h intervals, significant proliferation of DPSCs was seen in all samples, except for the NMTA which exerted toxic effects on cells. All of the three commercial MTAs and CEM cement showed comparative biocompatibility. However, NMTA had cytotoxic effects on DPSCs at all the time intervals.

Comparison of CT-Number and Gray Scale Value of Different Dental Materials and Hard Tissues in CT and CBCT.

Computed tomography (CT) and cone-beam CT (CBCT) are valuable diagnostic aids for many clinical applications. This study was designed to compare the gray scale value (GSV) and Hounsfield unit (HU) of selected dental materials and various hard tissues using CT or CBCT. Three samples of all test materials including amalgam (AM), composite resin (CR), glass ionomer (GI), zinc-oxide eugenol (ZOE), calcium-enriched mixture (CEM) cement, AH-26 root canal sealer (AH-26), gutta-percha (GP), Coltosol (Col), Dycal (DL), mineral trioxide aggregate (MTA), zinc phosphate (ZP), and polycarbonate cement (PC) were prepared and scanned together with samples of bone, dentin and enamel using two CBCT devices, Scanora 3D (S3D) and NewTom VGi (NTV) and a spiral CT (SCT) scanner (Somatom Emotion 16 multislice spiral CT);. Subsequently, the HU and GSV values were determined and evaluated. The data were analyzed by the Kruskal-Wallis and Mann-Whitney U tests. The level of significance was determined at 0.05. There were significant differences among the three different scanners (P<0.05). The differences between HU/GSV values of 12 selected dental materials using NTV was significant (P<0.05) and for S3D and SCT was insignificant (P>0.05). All tested materials showed maximum values in S3D and SCT (3094 and 3071, respectively); however, bone and dentin showed low/medium values (P<0.05). In contrast, the tested materials and tissues showed a range of values in NTV (366 to15383; P<0.05). Scanner system can influence the obtained HU/GSV of dental materials. NTV can discriminate various dental materials, in contrast to S3D/SCT scanners. NTV may be a more useful diagnostic aid for clinical practice.

Management of inflammatory internal root resorption in primary molar teeth by using calcium enriched mixture cement: A case report

Management of inflammatory internal root resorption in primary molar teeth by using calcium enriched mixture cement: A case report

The long-term effect of calcium hydroxide, calcium-enriched mixture cement and mineral trioxide aggregate on dentin strength.

Many of highly-alkaline dental materials have some adverse effects on physical properties of dentin. As basic substances, mineral trioxide aggregate (MTA), calcium hydroxide (CH) and the new endodontic material, calcium-enriched mixture (CEM) cement, may adversely affect dentin. The purpose of this in vitro study was to evaluate the effect of long-term application of CEM cement, MTA and CH on flexural strength of bovine dentin. Three hundred and twenty bovine dentin samples were divided into 4 groups, which were either exposed to CEM cement, CH, MTA or normal saline (control group). Samples of each group were divided into 4 subgroups which were tested by means of Instron Universal Testing Machine for periods of 7, 30, 180 and 365 days after exposure to the test materials. The required force for sample breakage was recorded. The data were analyzed by the two-way ANOVA and Tukey tests. The mean value of forces to break the samples in CEM cement and CH groups was significantly lower than the control group after 1 month (P<0.05). After 180 days, the samples of CEM cement group retrieved their strength but in MTA and CH groups the time interval weakened the samples. After one year of exposure to CH and MTA, flexural strength of the dentin reduced to 72% and 38.7%, respectively (P<0.05). Yet the flexural strength of samples in CEM cement group did not change significantly compared to control group. Following 365 days of application of experimental materials to bovine dentin, the CEM cement showed an interesting result and the samples in this group reached their initial strength during the first week of the study but the other materials caused a reduction in dentin strength at the end of the study.

Effect of Mineral Trioxide Aggregate, Calcium-Enriched Mixture Cement and Mineral Trioxide Aggregate with Disodium Hydrogen Phosphate on BMP-2 Production.

One of the hypotheses regarding the calcification induction by mineral trioxide aggregate (MTA) is the involvement of transforming growth factor-Beta (TGF-β) super family. Calcium-enriched mixture (CEM) cement is one of the endodontic biomaterials with clinical applications similar to MTA. The aim of the present in vitro study was to compare the induction of bone morphogenic protein-2 (BMP-2) by a combination of disodium hydrogen phosphate (DSHP) and tooth colored ProRoot MTA (WMTA), to that of CEM cement and WMTA. Human gingival fibroblasts (HGFs) were obtained from the attached gingiva of human premolars. HGFs were cultured in Dulbecco's Modified Eagle's medium, supplemented with 10% fetal calf serum, penicillin, and streptomycin. Cells in groups 1, 2 and 3 were exposed to WMTA, CEM and WMTA+DSHP discs, respectively. The fourth group served as the control. After 72 h of exposure, HGF viability was determined by Mosmann's tetrazolium toxicity (MTT) assay. BMP-2 levels in cell-free culture media were determined by enzyme-linked immunosorbent assay (ELISA). Statistical analysis was performed using the one-way ANOVA, followed by the post hoc Games-Howell test for BMP-2 and post hoc Tukey's test for the results of MTT assay. Cellular viability was significantly higher in group 3 compared to the other groups (P<0.05); however, CEM and WMTA did not exhibit significant differences (P=0.08). The control group exhibited significantly higher cellular viability in comparison to the other groups of the study (P<0.05). The highest and lowest protein production rates were observed in the WMTA (3167±274.46 pg/mL) and WMTA+DSHP (1796±839.49 pg/mL) groups, respectively. There were no significant differences between the control, WMTA and CEM groups (P>0.05). WMTA and CEM did not exhibit any significant differences in terms of inducing BMP-2 production; however, incorporation of DSHP into WMTA resulted in a decrease in the induction of this protein.