This study was aimed at revealing the influence of Al and Zn additions on microstructure, texture evolution and mechanical properties of twin roll casting Mg during multi-pass hot rolling. Firstly, both pure Mg and AZ31 sheets were rolled 9 passes with ∼80% thickness reduction. More effective grain refinement in AZ31 compared to pure Mg after hot rolling, which caused by the pinning effect from fine Mg17Al12 particles present in AZ31 alloy. Meanwhile a strong basal texture gradually formed with increasing thickness reduction in pure Mg. With Al and Zn adding, the texture intensity of AZ31 was much lower than pure Mg in each rolling-pass. The 5th AZ31 sample features a maximum intensity of ∼12.9, which is reduced by 50.6% as compared to the value of ∼26.1 for pure Mg. Compared to pure Mg, the Al and Zn solutes and weakened texture in AZ31 favor the strong work hardening, which promotes a simultaneous high ultimate tensile strength of ∼270 MPa and ductility of ∼22% in the 5th AZ31 sample. The results will be helpful for the TRCed Mg alloys with huge potential for industrial application.