Amount Of Organoclay Research Articles

The role of organically modified layered silicate in the breakup and coalescence of droplets in PBT/PE blends

In this study, we investigated the effect of organically modified nanoclay (organoclay) on the morphology of immiscible polymer blends (PBT/PE) with various compositions of PBT ranging from 1 to 90 wt%. When a small amount of organoclay between 1 and 3 phr is added to the blend, the thin clay tactoids of the thickness of the order of 10 nm are located at the interface between PBT and PE phase. As its content is increased, the additional organoclay positions in a specific component depending on its affinity with the component. The addition of a small amount of organoclay results in the effective size reduction for PBT/PE blend. The organoclay located at the interface forms the interfacial phase with a non-homogeneous distribution of clay along the interface and changes the interfacial tension, which result in the coalescence suppression of the droplets. Rigid organoclay with a high aspect ratio allows the blend morphology with long-term thermal stability by suppressing the Brownian motion. This ability of the organoclay to suppress the coalescence of the droplets effectively reduces the droplet size. On the other hand, additional organoclay results in the rheological properties of particular component being increased, which means the change in the viscosity ratio. The change in the viscosity ratio, together with the coalescence suppression effect, affects the determination of the droplet size, depending on the location of the organoclay. Therefore, the organoclay suppresses the coalescence of the droplets at the interface, while simultaneously influencing the breakup of the droplets due to the change of viscosity ratio.

Morphology, thermal and mechanical behavior of polypropylene nanocomposites toughened with poly(ethylene‐co‐octene)

AbstractRubber‐toughened polypropylene (PP) nanocomposites containing organophilic layered silicates were prepared by means of melt extrusion at 230 °C using a co‐rotating twin‐screw extruder in order to examine the influence of the organoclay and the addition of PP grafted with maleic anhydride (PPgMAH) as a compatibilizer on the morphological, mechanical and thermal properties. The mechanical properties of rubber‐toughened polypropylene nanocomposites (RTPPNCs) were studied through tensile, flexural and impact tests. Scanning electron microscopy (SEM) was used for investigation of the phase morphology and rubber particles size. X‐ray diffraction (XRD) was employed to characterize the formation of nanocomposites. The thermal properties were investigated by using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The dynamic mechanical properties were examined by using dynamic mechanical analysis (DMA). From the tensile and flexural tests, the optimum loading of organoclay in RTPP was found to be 6 wt%. The optimum loading of PPgMAH, based on the tensile and flexural properties, was also 6 wt%. The increase in the organoclay and PPgMAH content resulted in a severe embrittlement, manifested by a drop in the impact strength and tensile elongation at break. XRD studies revealed that intercalated RTPPNCs had been successfully prepared where the macromolecular PP segments were intercalated into the interlayer space of the organoclay. In addition, the organoclay was dispersed more evenly in the RTPPNC as the PPgMAH content increased. TGA results revealed that the thermal stability of the RTPPNC improved significantly with the addition of a small amount of organoclay. Copyright © 2006 Society of Chemical Industry

Natural rubber/poly(ethylene-co-vinyl acetate)-blend-based nanocomposites

Natural rubber (NR)/poly(ethylene-co-vinyl acetate) (EVA) blend–clay nanocomposites were prepared and characterized. The blend nanocomposites were prepared through the melt mixing of NR/EVA in a ratio of 40/60 with various amounts of organoclay with an internal mixer followed by compression molding. X-ray diffraction patterns revealed that the nanocomposites formed were intercalated. The formation of the intercalated nanocomposites was also indicated by transmission electron microscopy. Scanning electron microscopy, used to study the fractured surface morphology, showed that the distribution of the organoclay in the polymer matrix was homogeneous. The tensile modulus of the nanocomposites increased with an increase in the organoclay content. However, an increase in the organoclay content up to 5 phr did not affect the tensile strength, but the organoclay reduced this property when it was increased further. This study also indicated that a low silicate content dispersed in the blend matrix was capable of increasing the storage modulus of the material. The addition of the organoclay also increased the decomposition temperature of the NR/EVA blends. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 353–362, 2006

Barrier and Mechanical Properties of Poly(caprolactone)/organoclay Nanocomposites

AbstractIn this study, biodegradable poly(caprolactone) (PCL) hybrids with two types of organoclays: Cloisite 30B (30B) and Cloisite 93A (93A) have been prepared by melt mixing and their barrier performance to air permeation and mechanical properties were investigated. The hybrids of PCL/30B were found to be nanocomposites resulted from the strong interaction between organic modifier of 30B and PCL and those of PCL/93A were microcomposites. The barrier performance of PCL/30B nanocomposite film to air permeation was much more improved than pure PCL and PCL/93A microcomposites at low organoclay concentration. With the increase of organoclay content the permeability coefficient was also increased that could attributed to the extra tortuous pathway for gas permeation caused by organoclay exfoliation. The barrier behaviour of PCL/30B nanocomposites could be approximately described by a theoretical model developed for composites. The mechanical properties measurements showed that the reinforcement of organoclay 30B in nanocomposites is more significant than 93A in microcomposites. Both tensile modulus and tensile strength were increased in PCL/30B nanocomposites even at at low amount of organoclay without much loss of strain at break as compared to pure PCL. The significant improvements in both barrier and mechanical properties in PCL nanocomposites could be attributed to the fine dispersion state of organoclay 30B platelets in PCL matrix and the strong interaction between organic modifier of 30B and matrix molecules.

Nanocomposites Based on Liquid Crystalline Resins

ABSTRACT The intercalation and exfoliation of liquid crystalline resins (LCRs) in the presence of organophilic montmorillonite were investigated. Their properties were compared with those of pristine resin, as well as with those of nanocomposites based on a commercial epoxy resin containing the same amounts of nanoclays. It was demonstrated that the dispersion of inorganic fillers has a detrimental effect on thermal and mechanical properties if a liquid crystalline (LC) matrix is used. In particular, tensile strength of LC nanocomposites is reduced with the increasing amount of organoclay, which, somehow, disturb the molecular order in the liquid crystalline resin.

Crystallization characteristics of intercalated poly(L-lactide)/organo-modified montmorillonite hybrids

The crystallization behavior of intercalated Poly(L-lactide) (PLLA)/organo-modified montmorillonite hybrids has been investigated in term of growth of spherulites and bulk crystallization. The PLLA hybrids were prepared via melt-compounding between PLLA and montmorillonite organo-modified (organoclay) with two different types of ammonium salts: trimethyl octadecyl- or bis(4-hydroxy butyl) methyl octadecyl ammonium salts. The nucleation rate of PLLA crystallites is slightly enhanced by natural clay, while reduced by organoclay due to the shielding effect and/or miscibility between surfactants of clays and PLLA chains. The incorporation of small amount of organoclay in PLLA matrix shows a tendency to reduce slightly the growth rate and the overall crystallization rate of PLLA crystallites. The secondary nucleation theory was utilized to discuss the crystallization behavior of these hybrids. POLYM. ENG. SCI., 45: 000‐000, 2005. © 2005 Society of Plastics Engineers

Novel morphologies of poly(phenylene oxide) (PPO)/polyamide 6 (PA6) blend nanocomposites

Poly(phenylene oxide) (PPO)/polyamide 6 (PA6) (50/50 w/w) blend nanocomposites were prepared by melt mixing of PPO, PA6, and organically modified clay. The morphology of PPO/PA6 nanocomposite with various amounts of clay has been investigated using scanning electron microscope (SEM), transmission electron microscope (TEM), and wide-angle X-ray diffraction (WAXD). For the PPO/PA6 blend without clay, PPO is dispersed in the PA6 matrix with an average particle diameter of about 4.2μm. The domain size of the dispersed PPO phase is significantly decreased to about 1.1μm by adding a small amount of clay (2%). However, when the amount of organoclay is more than 5%, the matrix-domain structure is found to transform into the co-continuous morphology. The TEM observation shows that all the organoclay is dispersed only in the PA6 phase with a high degree of exfoliation and there is no any clay detectable in the PPO phase for the nanocomposites regardless of the amount of clay. It is considered that the dispersed clay platelets play an important role in the control of the PPO/PA6 blend morphology. Firstly, the selective localization of clay in PA6 phase changes the viscosity ratio of the PPO and PA6 phases. Therefore, clay has significant effects on the morphology of the polymer blend. Secondly, the high aspect ratio of the clay platelets prevents the coalescence of domains during melt mixing.

Organoclay–natural rubber nanocomposites synthesized by mechanical and solution mixing methods

AbstractThis investigation describes two methods to obtain rubber composites based on natural rubber (NR) and organophilic layered silicates. In order to improve the exfoliation and compatibilization of the organoclays with the rubber matrix, a new approach which involves swelling of the organoclays with an elastomer solution prior to compounding has been used. The effect of the addition during swelling of a coupling agent, namely bis(trietoxysilylpropyl)tetrasulfan (TESPT), on the behaviour of the composites was also investigated. The results show that a low amount of organoclay (10 phr) significantly improves the properties of natural rubber. This suggests a strong rubber–organoclay interaction which is attributed to a high degree of rubber intercalation into the nanosilicate galleries, as was confirmed from X‐ray diffraction. In addition, an ulterior improvement in the properties of the nanocomposites prepared by solution mixing is clearly observed, due to the better filler–rubber compatibility. An even further increase in the properties is observed by treating the silicate with a silane coupling agent. The silane functional groups modify the clay surface, thus reducing the surface energy, and consequently improving the compatibility with the rubber matrix. Copyright © 2004 Society of Chemical Industry

The effect of organoclay on the mechanical properties and morphology of injection‐molded polyamide 6/polypropylene nanocomposites

AbstractNanocomposites containing a thermoplastic blend and organophilic layered clay (organoclay) were produced by melt compounding. The blend composition was kept constant [polyamide 6 (PA6) 70 wt % + polypropylene (PP) 30 wt %], whereas the organoclay content was varied between 0 and 10 wt %. The mechanical properties of the nanocomposites were determined on injection‐molded specimens in both tensile and flexural loading. Highest strength values were observed at an organoclay content of 4 wt % for the blends. The flexural strength was superior to the tensile one, which was traced to the effect of the molding‐induced skin‐core structure. Increasing organoclay amount resulted in severe material embrittlement reflected in a drop of both strength and strain values. The morphology of the nanocomposites was studied by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy‐dispersion X‐ray analysis (EDX), and X‐ray diffraction (XRD). It was established that the organoclay is well dispersed (exfoliated) and preferentially embedded in the PA6 phase. Further, the exfoliation degree of the organoclay decreased with increasing organoclay content. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 175–189, 2004

Crystallization behavior and thermal stability of poly(trimethylene terephthalate)/clay nanocomposites

AbstractPoly(trimethylene terephthalate) (PTT)/montmorillonite (MMT) nanocomposites were prepared by the solution intercalation method. Two different kinds of clay were organomodified with an intercalation agent of cetyltrimetylammonium chloride (CMC). X‐ray diffraction (XRD) indicated that the layers of MMT were intercalated by CMC, and interlayer spacing was a function of the cationic exchange capacity of clay. The XRD studies demonstrated that the interlayer spacing of organoclay in the nanocomposites depends on the amount of organoclay. From the results of differential scanning calorimetric analysis, it was found that clay behaves as a nucleating agent and enhances the crystallization rate of PTT. The maximum enhancement of the crystallization rate for the nanocomposites was observed in nanocomposites containing about 1 wt % organoclay with a range of 1–15 wt %. From thermogravimetric analysis, we found that the thermal stability of the nanocomposites was enhanced by the addition of 1–10 wt % organoclay. According to transmission electron microscopy, the organoclay particle was highly dispersed in the PTT matrix without a large agglomeration of particles for a low organoclay content (5 wt %). However, an agglomerated structure did form in the PTT matrix at a 15 wt % organoclay content. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 2902–2910, 2003

Synthesis of Poly(butylene terephthalate) Nanocomposite by In-situ Interlayer Polymerization and Characterization of Its Fiber (I)

The nanocomposites with poly(butylene terephthalate)(PBT) incorporated between the montmorillonite (MMT) layers were synthesized from dimethyl terephthalate (DMT) and butane diol (BD) by using an in-situ interlayer polymerization approach. The PBT nanocomposites were melt spun at different organoclay contents to produce monofilaments. The existence of clay layers in the PBT was confirmed by using X-ray diffraction and transmission electron microscopy, and those layers were found to be disperse on a nanometer scale. The thermal properties of the layered structures of the hybrids were found to be more stable than those of pure PBT. These improved thermal properties of the nanocomposites might arise from an extensive and strongly bonded interface between the organic and the inorganic components. Moreover, the addition of only a small amount of organoclay was enough to improve the mechanical properties of the PBT hybrid fibers.

Poly(butylene terephthalate)/organoclay nanocomposites prepared by in situ interlayer polymerization and its fiber (II)

Intercalated nanocomposites with poly(butylene terephthalate) (PBT) incorporated between the montmorillonite layers were synthesized from dimethyl terephthalate and 1,4-butane diol by using an in situ interlayer polymerization. The PBT nanocomposites were melt-spun at different organoclay contents to produce monofilaments. The samples were characterized by using wide angle X-ray diffraction, electron microscopy, thermal analysis, and tensile testing. The extent of the clay layer in the PBT was confirmed by using X-ray diffraction and electron microscopy, and the clay layer was found to be highly dispersed on a nanometer scale. The addition of only a small amount of organoclay was enough to improve the thermo-mechanical properties of the PBT hybrid fibers. The hybrids were extruded with various draw ratios (DRs) to examine the tensile mechanical property of the fibers. At DR=1, the ultimate tensile strength of the hybrid fibers increased with the addition of clay up to a critical content and then decreased. However, the initial modulus monotonically increased with increasing amount of organoclay in the PBT matrix. When the DR was increased from 1 to 6, for example, the strength and the initial modulus values of the hybrids containing 3wt% organoclay decreased linearly.

Nanocomposites of poly(trimethylene terephthalate) with organoclay

AbstractTwo different kinds of clay were organomodified with cetylpyridinium chloride (CPC) as an intercalation agent. Poly(trimethylene terephthalate) (PTT)/organoclay nanocomposites were prepared by the solution intercalation method. Wide‐angle X‐ray diffraction (WAXD) indicated that the layers of clay were intercalated by CPC and the interlayer spacing was a function of the cationic exchange capacity (CEC) of the clay: the higher the CEC, the larger the interlayer spacing is. The WAXD studies showed that the interlayer spacing of organoclay in the nanocomposites depends on the amount of organoclay. From the results of differential scanning calorimetry analysis it was found that clay behaves as a nucleating agent and enhances the crystallization rate of PTT. The maximum enhancement of the crystallization rate for the nanocomposites was observed in nanocomposites containing about 5 wt % organoclay with a range of 1–15 wt %. The thermal stability of the nanocomposites was enhanced by the addition of 1–10 wt % organoclay as found from thermogravimetric analysis. The thermal stability of the PTT/organoclay nanocomposites was related to the organoclay content and the dispersion in the PTT matrix. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 3315–3322, 2003

The Nucleating Effect of Montmorillonite on Crystallization of PET/Montmorillonite Nanocomposite

Poly(ethylene terephthalate) (PET)/montmorillonite (MMT) nanocomposites were prepared by solution intercalation method. The clay was organo-modified with intercalation agent of cetyltrimetylammonium chloride (CMC). XRD showed that the layers of MMT were intercalated by CMC. Four nanocomposites with organoclay contents of 1, 5, 10, and 15 wt% were prepared by solution blending. XRD showed that the interlayer spacing of organoclay in the nanocomposites depends on the amount of organoclay. The nucleating effect of organoclay is investigated using differential scanning calorimetry (DSC) analysis. Clay behaves as a nucleating agent and enhances the crystallization rate of PET. Maximum enhancement in crystallization rate for the nanocomposites was observed in blends containing ca. 10 wt% of clay in the range of 1–15 wt%. According to transmission electron microscopy (TEM), the organoclay particle was highly dispersed in the PET matrix without a large agglomeration of particles for low organoclay content (5 wt%). Agglomerated structure did form in the PET matrix at 15 wt% organoclay content.

Poly(lactic acid) nanocomposites with various organoclays. I. Thermomechanical properties, morphology, and gas permeability

AbstractThe thermomechanical properties, morphology, and gas permeability of hybrids prepared with three types of organoclays were compared in detail. Hexadecylamine–montmorillonite (C16–MMT), dodecyltrimethyl ammonium bromide–montmorillonite (DTA‐MMT), and Cloisite 25A were used as organoclays in the preparation of nanocomposites. From morphological studies using transmission electron microscopy, most clay layers were found to be dispersed homogeneously in the matrix polymer, although some clusters or agglomerated particles were also detected. The initial degradation temperature (at a 2% weight loss) of the poly(lactic acid) (PLA) hybrid films with C16–MMT and Cloisite 25A decreased linearly with an increasing amount of organoclay. For hybrid films, the tensile properties initially increased but then decreased with the introduction of more of the inorganic phase. The O2 permeability values for all the hybrids for clay loadings up to 10 wt % were less than half the corresponding values for pure PLA, regardless of the organoclay. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 94–103, 2003

Synthesis and properties of polybenzoxazole–clay nanocomposites

A novel polybenzoxazole (PBO)/clay nanocomposite has been prepared from a PBO precursor, polyhydroxyamide (PHA) and an organoclay. The PBO precursor was made by the low temperature polycondensation reaction between isophthaloyl chloride (IC) and 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane with an inherent viscosity of 0.5 dl/g. The organoclay was formed by a cation exchange reaction between a Na +-montorillonite (Na +-Mont) clay and an ammonium salt of dodecylamine. The PHA/clay was subsequently thermal cured to PBO/clay. Both X-ray diffraction and transmission electron microscope analyzes showed that the organoclay was dispersed in the PBO matrix in a nanometer scale. The in-plane coefficient of thermal expansion (CTE) of PBO/clay film decreased with increasing amounts of organoclay. The CTE of PBO/clay film containing 7 wt% clay was decreased by 21% compared to the pure PBO film. Both of the glass transition temperature ( T g) and the thermal decomposition temperature of PBO/clay increased with increasing amounts of organoclay. The thermal decomposition temperature and the T g of PBO/clay containing 7 wt% clay increased to 12 and 16 °C, respectively.

Nanocomposites of polyurethane with various organoclays: Thermomechanical properties, morphology, and gas permeability* This paper is dedicated to Prof. Jung Il Jin of Korea University, Seoul Korea, on the occasion of his 60th birthday.

The properties of polyurethane (PU) nanocomposites with three different organoclays were compared in terms of their thermal stabilities, mechanical properties, morphologies, and gas permeabilities. Hexadecylamine–montmorillonite, dodecyltrimethyl ammonium–montmorillonite, and Cloisite 25A were used as organoclays for making PU hybrid films. The properties were examined as a function of the organoclay content in a matrix polymer. Transmission electron microscopy photographs showed that most clay layers were dispersed homogeneously into the matrix polymer on the nanoscale, although some particles of clay were agglomerated. Moreover, the addition of only a small amount of organoclay was enough to improve the thermal stabilities and mechanical properties of PU hybrid films, whereas gas permeability was reduced. Even polymers with low organoclay contents (3–4 wt %) showed much higher strength and modulus values than pure PU. Gas permeability was reduced linearly with an increasing amount of organoclay in the PU matrix. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 670–677, 2002; DOI 10.1002/polb.10124

Polyimide nanocomposite with a hexadecylamine clay: Synthesis and characterization

AbstractA poly(amic acid) was prepared by the reaction of 3,3′‐dihydroxybenzidine and pyromellitic dianhydride in N,N‐dimethylacetamide. Hexadecylamine was used as an organophilic alkylamine in organoclay. Cast films were obtained from blend solutions of the precursor polymer and the organoclay. The cast film was heat treated at different temperatures to create polyimide (PI) hybrid films. We set out to clarify the intercalation of PI chains to hexadecylamine–montmorillonite (C16–MMT) and to improve thermal and tensile properties and the gas barrier. It was found that the addition of only a small amount of organoclay was enough to improve both the thermal and the mechanical properties of PIs. Maximum enhancement in the ultimate tensile strength for PI hybrids was observed for the blends containing 4% C16–MMT. The initial modulus monotonically increased with further increases in C16–MMT content. Water vapor permeability was decreased with increasing clay loading from 1 to 8 wt %. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 2294–2301, 2002

Nanocomposites of polyurethane with various organoclays: Thermomechanical properties, morphology, and gas permeability*

AbstractThe properties of polyurethane (PU) nanocomposites with three different organoclays were compared in terms of their thermal stabilities, mechanical properties, morphologies, and gas permeabilities. Hexadecylamine–montmorillonite, dodecyltrimethyl ammonium–montmorillonite, and Cloisite 25A were used as organoclays for making PU hybrid films. The properties were examined as a function of the organoclay content in a matrix polymer. Transmission electron microscopy photographs showed that most clay layers were dispersed homogeneously into the matrix polymer on the nanoscale, although some particles of clay were agglomerated. Moreover, the addition of only a small amount of organoclay was enough to improve the thermal stabilities and mechanical properties of PU hybrid films, whereas gas permeability was reduced. Even polymers with low organoclay contents (3–4 wt %) showed much higher strength and modulus values than pure PU. Gas permeability was reduced linearly with an increasing amount of organoclay in the PU matrix. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 670–677, 2002; DOI 10.1002/polb.10124

Nanocomposites of poly(ethylene terephthalate‐co‐ethylene naphthalate) with organoclay

AbstractPoly(ethylene terephthalate‐co‐ethylene naphthalate) (PETN)/organoclay was synthesized with the solution intercalation method. Hexadecylamine was used as an organophilic alkylamine in organoclay. Our aim was to clarify the intercalation of PETN chains to hexadecylamine–montmorillonite (C16–MMT) and to improve both the thermal stability and tensile property. We found that the addition of only a small amount of organoclay was enough to improve the thermal stabilities and mechanical properties of PETN/C16–MMT hybrid films. Maximum enhancement in both the ultimate tensile strength and initial modulus for the hybrids was observed in blends containing 4 wt % C16–MMT. Below a 4 wt % clay loading, the clay particles could be highly dispersed in the polymer matrix without a large agglomeration of particles. However, an agglomerated structure did form in the polymer matrix at a 6 wt % clay content. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2581–2588, 2001