Abstract

Investigating Young's modulus at elevated temperatures supports the understanding of microstructural changes as a function of application temperature. A sintered alumina and three carbon‐bonded alumina materials with carbon contents of 20 and 30 wt% and alumina grain size of 0.6–3 mm were investigated. Young's modulus was measured in a temperature range from 25°C to 1450°C by the impulse excitation technique. The Young's modulus of carbon‐bonded materials increases up to 140% at 1450°C. After one cycle, a decrease of the Young's modulus up to 50% is registered at room temperature. There is a strong hysteresis behavior during one cycle. Thermal expansion measurements show highest expansion for the highest graphite content material. The expansion of alumina grains and graphite flakes, resulting in microcrack generation during cooling and microcrack healing during heating, is reflected in the registered values of the Young's modulus as a function of the temperature. It is assumed, that higher graphite amounts as well as coarse grains lead to lower sintering effects of the microstructure at elevated temperatures and as a result lower values of the Young's modulus have been registered.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.