Abstract
The influence of Sm addition on the microstructure and superconducting properties of Y-Ba-Cu-O (YBCO) bulk superconductors has been studied. Precursor powders YBa2Cu3O7-δ (Y-123), Y2O3 and CeO2 were enriched with different amounts of SmBa2Cu3Oy (Sm-123) or Sm2O3 powders with the aim to increase critical current density, Jc,by introducing additional pinning centers. YBCO bulk superconductors with SmBa2Cu3Oy (Y123-Sm) or Sm2O3 (Y123-SmO) powder addition were prepared by the optimized top seeded melt growth process in the form of single grains. Microstructure analysis revealed that Sm2O3 addition leads to a higher amount of smaller Y2BaCuO5 (Y-211) particles, what is related to high critical current densities (Jc ~ 7 x 104 A/cm2) of the YBCO samples with Sm2O3 addition in low magnetic fields. The effect of Sm addition in the form of SmBa2Cu3Oy as well as Sm2O3 powder on Y2BaCuO5 particle size, critical temperature, Tc, and critical current density, Jc, is reported.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.