Y2O3첨가량에 의한 Al2O3복합재 세라믹스의 균열 치유와 고온 굴힘강도 특성

Abstract

The four kinds of Al₂O₃ composite ceramics were prepared using a mixture of 85 wt.% Al₂O₃ (mean size 0.5 ㎛), 15 wt.% SiC powder with Y₂O₃ as an additive powder (0, 1, 3 and 5 wt.%). The crack-healing strengths were studied as functions of crack-healing temperature and amount of Y₂O₃. The in-situ crack-healing behavior was observed at 1,573 K for 1 h in the air. The heat treated specimen with 3 wt.% of Y₂O₃ showed better crack-healing ability than specimen with 1 or 5 wt.% of Y₂O₃. In case of specimen with 3 wt.% of Y₂O₃, the bending strength of the crack-healed specimen at 1,473 K was recovered to the bending strength of smooth specimen treated at 1573 K. The heat-resistance limit temperature of Al₂O₃ composite ceramics was 1,073 K, 1,373 K, 873 K for the specimen with 1, 3, 5 wt.% of Y₂O₃.