Abstract
Orientation, structure and morphology in the early growth stages of CuO films on strontium titanate were studied by synchrotron radiation X-ray diffraction. Nanostructured CuO films were obtained by ex situ heat treatment at 970 K in oxygen flow at ambient pressure after an initial deposition of Cu on SrTiO3(001) at 10−4 Pa oxygen pressure using the molecular beam epitaxy technique. These films at low coverages grow forming islands a few tens of nanometers wide, with the [010] direction perpendicular to the substrate surface. Two types of epitaxies are observed, CuO[001]//SrTiO3[100] and CuO[100]//SrTiO3[100], the former being the preferred one. The combination of these epitaxies with the P4mm surface symmetry of the substrate generates 16 different orientations of nanostructures. The lattice constant values obtained from X-ray diffraction are very close to those of bulk tenorite, with the exception of the monoclinic angle β, which is reduced from 99.54° to 96.76(8)° by the epitaxy constraints. This angle is a key parameter in determining the magnetic properties of CuO.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.