PurposeThis paper aims to invastigate of the wetting and interfacial properties of Sn-(3-x)Ag-0.5Cu-(x)Bi (x = 0.5, 1 and 2 in Wt.%) Pb-free solder alloys at various temperatures ( 250, 280 and 310°C) on Cu substrate in Ar atmosphere.Design/methodology/approachIn this study, new Sn-(3-x)Ag-0.5Cu-xBi systems, low Ag content quaternary lead-free solder alloys, were produced by adding 0.5, 1 and 2% Bi to the near-eutectic SAC305 alloy. The wetting angles of three new alloys, Sn-2.5Ag-0.5Cu-0.5 Bi(SAC-0.5 Bi), Sn-2Ag-0.5Cu-1Bi(SAC-1Bi) and Sn-1Ag-0.5Cu-2Bi(SAC-2Bi) were measured by sessile drop technique on the Cu substrate in argon atmosphere.FindingsIn accordance with the interfacial analyses, intermetallic compounds of Cu3Sn, Cu6Sn5, and Ag3Sn were detected at the SAC-Bi/Cu interface. The results of wetting tests show that the addition of 1 Wt.% Bi improves the wetting properties of the Sn-3Ag-0.5Cu solder. The lowest wetting angle (θ) was obtained as 35,34° for Sn-2Ag-0.5Cu-1Bi alloy at a temperature of 310 °C.Originality/valueThis work was carried out with our handmade experiment set and the production of the quaternary lead-free solder alloy used in wetting tests belongs to us. Experiments were conducted using the sessile drop method in accordance with wetting tests.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.