Abstract
This study utilizes two ion-implantation methods, plasma immersion ion implantation (PIII) and metal vapor vacuum arc (MeVVA), to prepare Ti–N phases on the surface of Ti–6Al–4V. By the nitrogen PIII method, both nitrogen and minor oxygen species are simultaneously attracted by the negatively charged substrate. The penetration of N and O interstitial elements to an extensible depth is possible owing to the effect from the negatively charged target. The nitrogen PIII treatment does not produce a novel Ti–N phase. As a result, the modified surface does not behave anticorrosive. The H n and the E determined by nanoindentation also remain unchanged. It is still potential to apply this non-directional treatment by increasing bias voltage of the target, coating pure titanium on Ti–6Al–4V, and adjusting the regeneration process of nitrogen ions. The MeVVA treatment creates a novel αTiN 0.3 (011) phase on Ti–6Al–4V in present study. It signifies that the interactions between kinetic Ti ions of varied energies and minor nitrogen molecules, with minor participation of oxygen, are highly feasible. The novel ion-implanted Ti–N phase is corrosion resistant, which is capable to reduce passivation current density by forming a passive film. Moreover, the MeVVA-treated surface is surface-hardened; the E is simultaneously increased. The increase of nano mechanical properties can be visualized by 3D images using Nano Vision and determined by analyzing the tip/surface impact structure on the indentation site.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call