Abstract
Friction and wear behavior of Al6061 monolithic alloy and 1wt% CNTs reinforced Al6061 composite prepared through ball milling and spark plasma sintering was investigated. It was found that, under mild wear conditions, the composite displayed lower wear rate and friction coefficient compared to the monolithic alloy. However, for severe wear conditions, the composite displayed higher wear rate and friction coefficient compared to the monolithic alloy. Analysis of worn surfaces revealed that, at lower loads, abrasion was the dominant wear mechanism for both materials. At higher loads, adhesion was found to be dominant for the monolithic alloy while excessive sub-surface fracturing and delamination were mainly observed for the composite. Also, it was clarified that the friction and wear behavior of Al–CNT composites is largely influenced by the applied load and there exists a critical load beyond which CNTs could have a negative impact on the wear resistance of aluminum alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.