Abstract
Petrochemical polyethylene waxes (Mn = 800-8000 g/mol for commercial Ziegler waxes) as additives, lubricants, and release agents are essential to numerous products and production processes. The biodegradability of this class of compounds when unintentionally released to the environment is molar mass dependent and subject to ongoing discussions, and alternatives to conventional polyethylene waxes are desirable. By employing bottom-up and top-down approaches, that is nonstoichiometric A2 + B2 polycondensation and chain scission, respectively, linear waxes with multiple in-chain ester groups as biodegradation break points could be obtained. Specifically, waxes with 12,12 (WLE-12,12, WLE = waxes linear ester) and 2,18 (WLE-2,18) carbon atom linear ester repeat unit motifs were accessible over a wide range of molar masses (Mn ≈ 600-10 000 g/mol). In addition to the molar mass, the type of end group functionality (i.e., methyl ester, hydroxy, or carboxylic acid end groups) significantly impacts the thermal properties of the waxes, with higher melting points observed for carboxylic acid end groups (e.g., Tm = 83 °C for carboxylic acid-terminated WLE-12,12 with Mn,NMR = 1900 g/mol, Tm = 92 °C for WLE-2,18 with Mn,NMR = 2200 g/mol). A HDPE-like orthorhombic crystalline structure and rheological properties comparable to a commercial polyethylene wax suggest WLE-12,12 and WLE-2,18 are viable biodegradable and biosourced alternatives to conventional, petrochemical polyethylene waxes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.