Abstract
Macroscopically long ropes of aligned single-walled carbon nanotubes (SWNTs), synthesized by a hydrogen and argon arc discharge method, were cold pressed into tablets without any binder for measurements of their volumetric hydrogen storage capacity. The typical apparent density of the tablets was measured to be around 1.7 g/cm3 with respect to a molding pressure of 0.75 Gpa. A volumetric and mass hydrogen storage capacity of 68 kg H2/m3 and 4.0 wt %, respectively, was achieved at room temperature under a pressure of 11 MPa for suitably pretreated SWNT tablets, and more than 70% of the hydrogen adsorbed can be released under ambient pressure at room temperature. Pore structure analysis indicated that the molding process diminished the mesopore volume of the SWNT ropes, but exerts little influence on their intrinsic pore textures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.