Abstract
To enhance the understanding of matrix cracking and damage progression on the macroscopic scale, within a 0/90° fibre reinforced SiCf/SiC ceramic matrix composite (CMC), X-ray computed tomography (XCT) imaging and analysis have been performed in conjunction with a commercially available in-situ mechanical loading device. CMC test coupons were subjected to tensile cyclic loads and inspected using XCT without removal from the tensile loading device. Attempts to measure and quantify the resulting damage using volumetric image analysis techniques are presented, by characterising the crack network from XCT images acquired at both the maximum and minimum load condition during selected fatigue cycles. The XCT detection of significant crack development within the first loading half-cycle shows good agreement with cumulative acoustic emission energy data recorded under similar test conditions. The results are seen as an important step towards correlating the damage behaviour detected via different NDE and health monitoring techniques.
Accepted Version (
Free)
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call