Abstract
A vanadium dioxide (VO2) thin film was prepared on an Al-doped ZnO (AZO) conductive glass substrate by DC magnetron sputtering and a post-annealing process. The AZO/VO2/AZO sandwiched structure was fabricated on the VO2/AZO composite film using photolithography and a chemical etching process. The composition, microstructure and optical properties of the VO2/AZO composite film were tested. The results showed that the VO2/AZO composite film was poly-crystalline and the AZO layer did not change the preferred growth orientation of VO2. When the voltage was applied on both of the transparent conductive layers of the AZO/VO2/AZO sandwiched structure, an abrupt change in the current was observed at different temperatures. The temperature dependence of I–V characteristic curves for the AZO/VO2/AZO sandwiched structure was analyzed. The phase transition voltage value is 7.5V at 20°C and decreases with increasing temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.