Abstract
Broad visible emission at the wavelength range of 400–800nm was obtained at room temperature in amorphous barium titanate (BaTiO3) nanofibers, which were prepared by electrospinning and calcined at low temperatures. Structure and morphology of the BaTiO3 nanofibers were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM), thermo-analysis and Raman spectroscopy. XRD data shows that the BaTiO3 nanofibers calcined at temperatures below 650°C are amorphous, in which intense photoluminescence (PL) emission bands at 600nm have been detected. More importantly, PL performance of the BaTiO3 nanofibers exhibited a strong dependence on the calcination temperature. Observable emission was only found in the low-temperature treated fibers. Mechanism of the observed photoluminescence has been discussed. The achievements shown herein may be help to find new light-emitting materials.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.