ABSTRACT Formation of ultrafine iron powders by vapor-phase reduction of ferrous chloride with hydrogen was studied in a tubular reactor made of quartz, 3.5 cm in diameter and 1.5 m in length. Effects on the particle-size distribution of produced iron powders were investigated of various operating variables including the temperature in reaction zone, the concentration of FeCl2, and the flow rate of dilution argon gas. Ultrafine iron powders ranging from 40 to 88 nm in average particle size were produced. The geometric standard deviation was about 1.4. Particles were linked to each other to form a chain, probably due to magnetic interaction. By electron diffraction, all the particles are found to be single crystal. Over the reaction zone temperature ranging from 800 to 950°C, the average size of primary particles decreased with temperature, probably due to enhanced nucleation rate. No significant change in the particle size was observed for a reduction of reactor residence time by one-third. The coercive f...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.