Abstract
Vanadium extraction from titano-magnetite by using hydrofluoric acid was put forward. The process of low intensity magnetic separation, hydrofluoric acid leaching, co-precipitation with NaOH, roasting with Na2CO3, circulating water leaching and precipitation of vanadium has been investigated. The results show that over 85% vanadium could be directly leached under the condition of sulfuric acid concentration of 5mol/L, CaF2 dosage of 5%, leaching temperature of 95°C, leaching time of 3h and liquid to solid ratio of 3mL/g. With the pH value of 4.5, temperature of 40°C and time of 30min, the co-precipitation rate of vanadium in the acid leaching solution was over 99%. The water leaching rate of vanadium of the co-precipitation reached 95% under the condition of roasting temperature of 800°C, Na2CO3 dosage of 6%, roasting time of 1h, leaching temperature of 90°C, leaching time of 40min, liquid to solid ratio of 2mL/g and leaching stage of 4. Finally, the total recovery of vanadium could reach 81% and the purity of the product V2O5 was 99.65% meeting the standard specification with precipitation of vanadium and calcination.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.