Abstract
While aluminum alloys are widely used in industrial applications, their protection by anodization as surface treatment always requires a preparation step by alkaline or acid etching. In this paper, use of ultrasound during the acid etching step on the 2024 aluminum alloy was investigated. Etching rate, calculated as of weight loss, was measured under ultrasound irradiation, and compared to silent conditions. The etched surface was characterized by Scanning Electron Microscopy/Energy Dispersive X-ray Spectroscopy (SEM/EDS) and X-Ray Diffraction (XRD). Surface treatment was performed up to the final anodization step samples, and their final properties were evaluated as a function of various pre-treatments, including acid etching under ultrasound. The main evaluation concerned anticorrosion properties through electrochemical tests: polarization measurements and electrochemical impedance spectroscopy (EIS) in NaCl solution. Finally, use of ultrasound irradiation during acid preparation induced a beneficial effect on the corrosion performance of the anodic layer.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.