Abstract
The preparation conditions for barium titanate zirconate [Ba(Ti0.70Zr0.30)O3] ceramics by the combustion method were studied. The X-ray diffraction pattern indicated that the calcined powders belonged to a cubic phase. The maximum percentage of the cubic perovskite phase was found in the sample calcined at 850°C. A pure cubic crystal structure was found in all ceramic samples. The average grain size increased with increasing sintering temperatures. The dielectric constant-temperature plots showed a maximum peak value of 5800 from ceramic sintered at 1350°C. The densities of samples corresponded to the dielectric constant. A diffuse phase transition was also observed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.