Usability of Trabzon stone as a natural building stone and aggregate

Abstract

This study investigated the suitability of Trabzon stone, which is used as a building stone in many areas in and around Trabzon province, as an aggregate. It was found that the uniaxial compressive strength values of the samples taken from the quarry were 87-130 MPa, P-wave velocities were 5048-5642 m/s, density value was 2.58 g/cm3, apparent porosity values were 2.77-4.54%, water absorption values by weight were 1.04-1.78% and water absorption value by mass was 2.0%. Weight loss in the freeze-thaw test was 0.36%, weight loss in the wet-dry test was 0.22%, loss in the magnesium sulfate test was 13%, Los Angeles fragmentation resistance in coarse aggregate was 22%, abrasion resistance value was 18% and methylene blue value was 0.9%. When the results were analyzed, it was found that the mass water absorption rate and the magnesium sulfate test results were above the values required by the standards. Although these rocks are used as marble, it has been determined that the waste material is not suitable for use as ballast, crushed stone, stone fill, pere, and masonry for road and concrete construction. Despite this result, it is necessary to investigate the usability of materials from other marble quarries in the region as aggregates.