Abstract
Electrospinning was used to fabricate beadless microfibrous polyacrylonitrile (ePAN) mats with an average fiber diameter of 1448±380nm from a 10wt.% PAN in dimethylformamide (DMF) dope solution at applied voltage of 18kV and 20cm fiber collection distance. Urease (EC 3.5.1.5) was then covalently immobilized on dispersed microfibrous ePAN mats following the chemical treatment of fibers with ethylenediamine (EDA) and glutaraldehyde (GA). The optimal concentration of GA for immobilization was 5%. The amount of loaded urease reached 157μg/mg mat, exhibiting 54% of the free urease activity. The surface chemistry of as-spun and chemically treated fibers was examined with Fourier transform infrared (FTIR) spectroscopy. Field emission scanning electron microscopy (FESEM) was used to study the morphology and diameter of the pristine, chemically treated, and urease-immobilized microfibrous mats. Immobilized urease showed increased temperature for maximum activity (from 37 to 50°C for free and immobilized urease, respectively) and improved storage stability (20days). The immobilized urease was also less sensitive to the changes in pH, especially in acid conditions. In addition, nearly 70% of initial activity of the immobilized urease was retained after 15 cycles of reuse, which proved the applicability of the electrospun fibers as successful enzyme carriers.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.