Upconversion luminescence and temperature sensing properties of Ho3+,Yb3+-codoped Bi2WO6.

Abstract

Ho3+ and Yb3+-codoped Bi2WO6 upconversion luminescent materials at different concentrations were prepared via a high-temperature solid-phase method. The X-ray diffraction patterns showed that Ho3+ and Yb3+ doping basically did not affect the orthorhombic crystal system structure of the Bi2WO6 matrix material. Scanning electron microscopy images showed that 3%Ho3+,10%Yb3+:Bi2WO6 consisted of irregular bulk particles with sizes in the range of 0.5-2 μm and some powder agglomeration. SEM mapping and EDS measurements of the powder showed that the elements were relatively uniformly distributed. Under 980 nm excitation, the emission intensity of Ho3+ was the largest for the 3%Ho3+- and 10%Yb3+-doped sample. With an excitation power ranging from 45 mW to 283 mW for the 3%Ho3+,10%Yb3+:Bi2WO6 sample, the relationship between the luminescence intensity and pump power was determined; the results indicated that the Ho3+ (538 nm, 546 nm, 660 nm, 756 nm) emission peaks originated from two-photon absorption. In the temperature range of 298 K-573 K, under 980 nm laser excitation, the maximum absolute temperature sensitivity Sa was 0.029% K-1 (373 K), the maximum relative temperature sensitivity Sr was 0.034% K-1 (348 K) for the Ho3+ thermally coupled energy levels 5F4/5S2, and the minimum temperature resolution δT was 1.2857 K (298 K). Under the same conditions, the maximum Sa was 51.02% K-1 (573 K), the maximum Sr was 1.85% K-1 (523 K) for the Ho3+ nonthermally coupled energy levels 5F5/5F4, and the minimum δT is 0.2477 K (448 K). The colour coordinates showed that the luminescence of the 3%Ho3+,10%Yb3+:Bi2WO6 sample gradually shifted from the green region to the red region with increasing temperature.