Abstract
The directionally solidified specimens of Nb-13.52 Si-22.60 Ti–6.88 Hf–2.54 Cr–2.24 Al alloy were prepared in an electron beam floating zone melting furnace at the withdrawing rate of 0.1, 0.3, 0.6, 1.0, 2.4 and 6.0 mm/min. All the primary Nb solid solution (Nbss) columns, Nbss + (Nb)3Si/(Nb)5Si3 eutectic colonies and divorced (Nb)3Si/(Nb)5Si3 plates or chains align well along the longitudinal axis of the specimens. With increasing of the withdrawing rate, the microstructure is gradually refined, and the amount of Nbss + (Nb)3Si/(Nb)5Si3 eutectic colonies increases. Both the room temperature ultimate tensile strength σb and fracture toughness KQ are improved for the directionally solidified specimens. The tensile fracture occurs in a cleavage way.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.