Abstract
The microstructure and mechanical properties including room temperature fracture toughness Kq, tensile strengthσb and elongationδ at 1250°C of the Nb based alloy directionally solidified in an electron beam floating zone melting (EBFZM) furnace have been evaluated. The microstructure is primarily composed of Nb solid solution (Nbss), α-(Nb)5Si3 and (Nb)3Si phases. After directional solidification with the moving rate of electron beam gun R being respectively 2.4, 4.8 and 7.2 mm/min, the primary Nbss dendrites, Nbss + (Nb)5Si3/(Nb)3Si eutectic colonies (lamellar or rod-like) and divorced Nb silicide plates align along the longitudinal axes of the specimens. When R = 2.4 mm/min, the best directional microstructure is obtained. Directional solidification has significantly improved theσb at 1250°C and Kq. The maximumσb occurs for the specimens with R = 2.4 mm/min and is about 85.0 MPa, meanwhile, the Kq is about 19.4 MPam1/2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.