Abstract
Combining the intermetallic compound with the ductile metal at the eutectic composition is one promising method to improve the ductility of the intermetallic compound. This paper reports the microstructure and the micro-hardness of the Ni–Ni3Si eutectic in situ composites prepared by electron beam floating zone melting technique. Ni–Ni3Si eutectic in situ composites display regular lamellar eutectic structure at the solidification rate R=0.3–4.0mm/min. The lamellar spacing is decreased with the increase of the solidification rate. The phase composition of the Ni–Ni3Si eutectic in situ composites is also determined by X-ray diffraction. Ni–Ni3Si eutectic in situ composites present lower micro-hardness than pure Ni3Si, although a small quantity of metastable Ni31Si12 phase is formed during the directional solidification process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.