Ultranarrow Bandgap Naphthalenediimide-Dialkylbifuran-Based Copolymers with High-Performance Organic Thin-Film Transistors and All-Polymer Solar Cells.

Abstract

A new polymer acceptor poly{(N,N'-bis(2-ethylhexyl)-1,4,5,8-naphthalenedicarboximide-2,6-diyl)-alt-5,5-(3,3'-didodecyl-2,2'-bifuran)} (NDI-BFR) made from naphthalenediimide (NDI) and furan-derived head-to-head-linked 3,3'-dialkyl-2,2'-bifuran (BFR) units is reported in this study. Compared to the benchmark polymer poly(naphthalenediimide-alt-bithiophene) (N2200), NDI-BFR exhibits a larger bathochromic shift of absorption maxima (842 nm) with a much higher absorption coefficient (7.2 × 104 m-1 cm-1 ), leading to an ultranarrow optical bandgap of 1.26 eV. Such properties ensure good harvesting of solar light from visible to the near-infrared region in solar cells. Density functional theory calculation reveals that the polymer acceptor NDI-BFR possesses a higher degree of backbone planarity versus the polymer N2200. The polymer NDI-BFR exhibits a decent electron mobility of 0.45 cm2 V-1 s-1 in organic thin-film transistors (OTFTs), and NDI-BFR-based all-polymer solar cells (all-PSCs) achieve a power conversion efficiency (PCE) of 4.39% with a very small energy loss of 0.45 eV by using the environmentally friendly solvent 1,2,4-trimethylbenzene. These results demonstrate that incorporating head-to-head-linked BFR units in the polymer backbone can lead to increased planarity of the polymer backbone, reduced optical bandgap, and improved light absorbing. The study offers useful guidelines for constructing n-type polymers with narrow optical bandgaps.