Abstract
ABSTRACT Ultra-low cycle fatigue (ULCF) tests of corroded steel specimens were conducted to illustrate the effects of corrosion on the ULCF properties and fracture mechanism of structural steel. Fatigue crack initiation and propagation process and fracture morphology were observed respectively. The results indicate that the ULCF fracture life of corroded specimens decreases more with increasing surface roughness. The crack-initiation life of corroded specimens is less than half of the fracture life. With corrosion degree increases, the area of the ULCF crack propagation zone expands observably, where it gets harder to find dimples, indicating a transition from ductile to brittle fracture mode.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.