Abstract
Varying amounts of Co and Ni were substituted into the metal–organic framework Mg-MOF-74 via a one-pot solvothermal reaction, and the effects of these substitutions on CO2 adsorption and kinetic water stability properties were examined. Based on elemental analyses, Co and Ni are more favorably incorporated into the MOF-74 framework from solution than Mg. In addition, reaction temperature more strongly impacts the final metal composition in these mixed-metal (MM) MOF-74 structures than does the reaction solvent composition. Single-component CO2 adsorption isotherms were measured for the MM-MOF-74 systems at 5, 25, and 45 °C, and isosteric heats of adsorption were calculated. These results suggest that CO2 adsorption properties can be adjusted by partial metal substitution. Water adsorption isotherms were also measured for the MM-MOF-74 samples, with powder X-ray diffraction patterns and Brunauer–Emmett–Teller surface areas measured both before and after water exposure. Results show that Mg-MOF-74 can gain ...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.