Abstract
In this paper, vinyl-capped silica nanoparticles (V–SiO2) were first synthesized from tetraethyl orthosilicate (TEOS) and vinyltriethoxysilane (VTEOS). Then the V–SiO2 nanoparticles were modified with poly(methylhydrosiloxane) (PMHS) and allyl-poly(ethylene glycol) (APEG) to form core-shell hybrid particles V–SiO2/PMHS/APEG, which showed tunable wettability as well as uniform monodispersity in ethanol and toluene. Particularly, V–SiO2/PMHS/APEG samples with moderate wettability could be served as emulsion stabilizer for silicone oil–water system. The modified particles were characterized by static contact angle (CA), Fourier transform infrared (FT-IR) spectroscopy, FT–Raman spectroscopy, 29Si CP MAS NMR, thermal analysis (TGA), transmission electron microscopy (TEM) and particle size distribution. FT-IR, FT–Raman and 29Si CP MAS NMR demonstrated that PMHS together with APEG was chemically anchored to the surface of nano-SiO2. Deduced from static contact angle, strong hydrophobicity (CA=157.76°) could be achieved for V–SiO2/PMHS particles (m(PMHS):m(V–SiO2)=1:1), while V–SiO2/PMHS/APEG samples exhibited moderate wettability (CA=89.20°) when the mass ratio of V–SiO2, PMHS and APEG was conducted at 1:1:6.0. Thermal analysis (TGA) showed that the grafting yield of PMHS and APEG was 5.76×10−5 and 6.13×10−4mol/g, respectively. V–SiO2/PMHS/APEG samples displayed superior monodispersity in both ethanol and toluene, and the mean diameter was 245.5nm, revealed from particle size distribution. Furthermore, digital photos, optical micrographs and emulsion drop size distribution demonstrated that silicone oil/water emulsions were successfully stabled by the core-shell hybrid particles V–SiO2/PMHS/APEG.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Colloids and Surfaces A: Physicochemical and Engineering Aspects
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.