Abstract
The neutron multiplier lead (Pb) containing Li2TiO3-0.5Li4SiO4–Pb was prepared, which aimed at the improvement of the tritium release performance of the lithium ceramic without an increase in lithium density. Li2TiO3-0.5Li4SiO4–Pb and that without Pb were irradiated at Kyoto University Research Reactor (KUR) with the thermal neutron flux of 5.5 × 1012 n s−1 cm−2 and the fast neutron flux of 1.2 × 1012 n s−1 cm−2. Fast neutrons can trigger the Pb (n, 2n) reaction. The tritium release experiments were conducted using the tritium thermal desorption spectroscopy (tritium-TDS) system. Compared with Li2TiO3-0.5Li4SiO4, the tritium release rate at the lower temperature range was higher than that for Li2TiO3-0.5Li4SiO4–Pb. The tritium-TDS spectrum was also shifted to the lower temperature side. The isothermal heating experimental results confirmed that tritium in the form of gas species (HT) was controlled by the diffusion process, while the trapping and de-trapping process contributed to the total tritium release. Further, 3 keV D2+ implantation with the fluence of 2.0 × 1022 D m−2 and subsequent TDS measurements were performed. It was shown that the D2 release at the lower temperature side was increased for Li2TiO3-0.5Li4SiO4–Pb. Meanwhile, HD and HDO release at higher temperature side was significantly decreased.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.