Abstract
The aim of this research is to determine the effect of sodium hydroxide molarity 2M combined with variations in slag percentage, ratio of alkali activator to binder (Al/Bi), and ratio of sodium silicate to sodium hydroxide (SS/SH) on the transport properties of fly ash-slag-based GPC cured at ambient temperature. The result is increase in slag percentage and SS/SH ratio lead to a decrease in porosity, water absorption rate and chloride permeability. The alkali activator to binder (Al/Bi) ratio of 0.45 produces the lowest porosity, water absorption rate, and chloride permeability. The porosity, sorptivity, and chloride penetration depths of all GPC are lower than those of OPC. The recommended mix compositions for GPC that exhibit lower transport properties than OPC are GPC4 (slag 40%, SS/SH ratio 1.5, Al/Bi ratio 0.45); GPC5 (slag 50%, SS/SH ratio 1.5, Al/Bi ratio 0.45); and GPC7 (slag 30%, SS/SH ratio 2.0, Al/Bi ratio 0.45).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.