Abstract
IntroductionThe aim of this study was to evaluate torsional, dynamic, and static cyclic fatigue resistance of the reciprocating One RECI (OR; Micromega, Besançon, France), WaveOne Gold (WOG; Dentsply Maillefer, Ballaigues, Switzerland), rotary One Curve (OC, MicroMega), and ProTaper Next X2 (PTN X2; Dentsply Sirona, Charlotte, NC) instruments. MethodsA total of 120 OR (n = 30), WOG (n = 30), OC (n = 30), and PTN X2 (n = 30) nickel-titanium instruments were used. Torque and rotation angle until failure under static torsion loading were measured according to ISO 3630-1. Static and dynamic fatigue resistance was measured as the time to fracture in an artificial stainless steel canal with a 60° angle and 5-mm radius of curvature at intracanal temperature. The results were analyzed with 1-way analysis of variance and the post hoc Tukey test. The alpha-type error was set at 5%. Fracture instruments from torsion and fatigue tests were examined with a scanning electron microscope. ResultsOR showed higher static fatigue resistance and rotation angle at fracture than WOG, OC, and PTN X2 (P < .05). WOG exhibited higher torsional resistance than the others (P < .05). The cyclic fatigue tests in dynamic mode had higher TTF than static for the PTN X2 and WOG groups (P < .05). In the dynamic tests, OR and WOG showed higher TTF than OC and PTN X2 (P < .05). ConclusionsUnder these experimental conditions, One RECI exhibited suitable mechanical properties with the highest cyclic fatigue resistance and angle of rotation among the tested instruments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.