TiSi2thickness limitations for use with shallow junctions and SWAMI or LOCOS isolation

Abstract

We have examined the impact of TiSi <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> formation on the properties of shallow n <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> and p <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> junctions (0.17-0.20 µm) in Si. The deposited Ti thickness varied from 300 to 1000 Å. The p <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> junctions developed high leakage currents after a reaction with Ti of initial thickness greater than 700 Å while the n <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> junctions were not degraded. In these studies LOCOS isolation was used and the TiSi <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> was formed away from the island edges. Additional experiments were performed on n <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> and p <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> diodes using SWAMI isolation with the TiSi <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> formed right up to the edges of the isolation. From step-height, spreading resistance, and RBS measurements, it was found that the thickness of TiSi <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> formed on n <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> Si was less than on p <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> Si for a given initial Ti thickness. The amount of electrically active dopant remaining in the substrates was seen to decrease with increasing Ti thickness. The result was supported by SIMS measurements, which also showed an accumulation of atomic fluorine at the TiSi <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> interface (on p <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> diodes only). Cross-sectional transmission electron microscopy was used to examine the silicide morphology and interface planarity.