Abstract
Tin oxide has been demonstrated as an ideal material for fabricating p-type and n-type thin film transistors (TFTs) for transparent CMOS type device fabrication. Both p and n-type conduction was observed in the thin films, prepared from metallic tin target by simply varying the oxygen flow rate during RF magnetron sputter deposition. Films deposited at room temperature were amorphous in nature, which after annealing at 200°C in air, crystallized to SnO and/or SnO2 phases. The TFTs fabricated on thermally oxidized silicon substrates showed high field effect mobility of 4.13 and 16 cm2/Vs with drain current on-off ratio 6 × 102 and 107 respectively for SnO p-type and SnO2 n-type TFTs. These are the highest values for p-type and n-type oxide TFTs fabricated from same source material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.