Abstract
Titanium nitride (TiN) nanoparticles hybridized with Fe and N co-doped carbon nanosheets (Fe-N-CNS) composite is constructed by a facile in-situ self-template strategy. During the low-temperature pyrolysis process, uniformly TiO2 nanoparticles were formed and anchored into Fe-doped carbon nitride nanosheets. After further high-temperature pyrolysis, Fe-doped carbon nitride nanosheets as self-template could decompose to form Fe-N co-doped carbon nanosheets and TiO2 nanoparticles were transferred into TiN nanoparticles during the high-temperature nitriding treatment. As a result, TiN nanoparticles hybridized with Fe-N-CNS composites (TiN/Fe-N-CNS) exhibit excellent ORR activity with more positive half-wave potential (0.87 V) and large limiting current density (4.43 mA cm−2) as well as high selectivity (electron transfer number around 4) for ORR in alkaline media. Moreover, it also shows higher stability and better methanol tolerance than those of commercial Pt/C catalyst in both alkaline and acidic media. This excellent ORR performance is attributed to the enhanced specific surface area and synergistically promotion effect of uniformly dispersed TiN on Fe-N-CNS.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.