Abstract
ABSTRACTThe time resolved and DC photoconduction characteristics of Si nanowire devices are described. Si nanowires with diameters ranging from 20-100 nm were grown using the vapor-liquid-solid (VLS) growth mechanism under standard conditions and devices were fabricated in a back-gate field effect transistor (FET) configuration using simple photolithography. It is shown that under certain biasing conditions, illumination with light from light emitting diodes with wavelengths ranging from 480 nm to 625 nm causes changes in current as high as 4%. On the other hand, illumination by a broadband incandescent source causes a ∼4.1% percent change in current. Photoconductive decay curves show bi- and tri-exponential behavior, indicative of multiple potential recombination mechanisms occurring within the Si nanowire devices. p-n doped Si nanowires show similar behavior. Studies under various drain and gate voltages provides insight into the proposed mechanism. It is argued that the Shottky barrier plays a strong role in the observed photoconduction process in these wires, as do transitions involving surface and deep level trap states.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.