Abstract
Electron-beam-deposited Ti∕Au ohmic contacts on undoped (n∼1017cm−3) bulk ZnO substrates exhibited as-deposited specific contact resistivity of 3×10−4Ωcm2, regardless of the polarity (Zn face or O face) of the ZnO substrate. The annealing environment (air or N2) also had no significant effect on contact properties. The specific contact resistivity slightly decreased after annealing at 300 °C but started to increase above 350 °C. The measurement temperature dependence of specific contact resistivity revealed that the dominant current transport mechanism is field emission even in the moderately doped ZnO. As the annealing temperature increased, some voids were observed on the metal surface, possibly due to reaction of Ti∕Au metallization and the evaporation of the oxygen from the ZnO substrate.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.