Abstract
AbstractHydrogenated amorphous silicon (a-Si:H) thin-film transistors (TFTs) are widely used in many areas and the most important application is in active matrix liquid crystal display. However, the instability of the a-Si:H TFTs constrains their usability. These TFTs have been annealed at higher temperatures in hope of improving their electrical performance. But, higher anneal temperatures become a constraint when the TFTs are grown on polymer-based flexible substrates. This study investigates the effect of anneal time on the performance of the a-Si:H TFTs on PEN. Thin-film transistors are annealed at different anneal times (4 h, 24 h, and 48 h) and were stressed under different bias conditions. Sub-threshold slope and the off-current improved with anneal time. Off-current was reduced by two orders of magnitude for 48 hours annealed TFT and sub-threshold slope became steeper with longer annealing. At positive gate-bias-stress (20 V), threshold voltage shift (∆Vt) values are positive and exhibit a power-law time dependence. High temperature measurements indicate that longer annealed TFTs show improved performance and stability compared to unannealed TFTs. This improvement is due to reduction of interface trap density and good a-Si:H/insulator interface quality with anneal time.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.