Abstract
Zeolite catalysts have shown significant advantages in hydrogenation reactions due to their ordered pore structure and abundant acid sites. Common zeolites exhibit pore accessibility limited to microporous states, which restricts their application in diffusion-limited processes. In this study, a steam-seeding-assisted colloidal crystal template (SSAC) method was used to prepare ZSM-5 zeolite with a three-dimensionally ordered macroporous (3DOM) structure, which was then loaded with nickel phosphide for hydrodenitrogenation reactions. SEM and TEM characterization demonstrated that the prepared zeolite material possessed a highly ordered 3DOM structure with interconnected macropores. XRD, FT-IR, and BET analysis indicated that the macroporous zeolite material exhibited a typical MFI structure, mesoporous channels, and a higher specific surface area. The high external surface area facilitated the formation of uniformly sized Ni2P nanoparticles on the zeolite surface. The introduction of macroporous structures also leads to suitable Brönsted acid and Lewis acid sites in zeolite materials. The resultant Ni2P/3DOMZSM-5 catalyst exhibited higher reaction rate constants and TOF (10.87×10−2 μmolg−1s−1 and 1.5×10−3s−1, respectively) compared to other zeolite catalysts and commercial catalysts.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.