Abstract
The effects of thickness of a-Si thin films on the resulting microstructure of metal-induced laterally crystallized (MILC) poly-Si and electrical characteristics of MILC low temperature poly-Si (LTPS) thin film transistors (TFTs) were investigated. The TEM images revealed a double-layer structure in the 1000-Å MILC poly-Si thin film. However, for the 400-Å MILC poly-Si thin film, there were single-layer grains within the thin film layer. The reason has been ascribed to the geometry restriction in the crystallization procedure. The average mobility of fabricated MILC LTPS TFTs with active layer thickness of 400 Å showed a little higher than that with 1000 Å active layer. Moreover, the MILC LTPS TFTs with active layer thickness of 400 Å exhibited better electrical uniformity than those with 1000 Å active layer either in threshold voltage or field-effect mobility. The reason should also be attributed to the different crystalline structures within the two thin-film layers. © 2003 The Electrochemical Society. All rights reserved.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.