Thermoreversible supramolecular polymer gels were prepared via metal–ligand coordination by mixing a poly(4-vinylpyridine)-b-poly(ethyl acrylate)-b-poly(4-vinylpyridine) (P4VP–PEA–P4VP) triblock copolymer and zinc chloride (ZnCl2) in a hydrophobic ionic liquid, 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imidide. FT-IR spectroscopy revealed metal–ligand coordination between zinc in ZnCl2 and pyridine groups as ligands on P4VP blocks, even in an ionic liquid. Thermoreversible viscoelastic properties between a semisolid (gel-like) state and a liquid-like state were confirmed by temperature-ramp oscillatory shear measurements. It was also revealed that thermoreversibility of supramolecular polymer gels depended strongly on stoichiometry between ligands and metals, where the maximum of storage modulus-loss modulus crossover temperature (Tgel) as an indicator of gelation was achieved when a molar amount of available coordination sites was a certain excessive amount (coordination site/ligand ratio ∼1.6). The molar ratio at the maximum Tgel is nearly independent of the number of ligands per triblock copolymer. On the other hand, the number of ligands per triblock copolymer affected the Tgel, where a larger number of ligands per triblock copolymer gave a higher Tgel, regardless of almost the same molecular weight of triblock copolymers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.