Abstract
The thermal behaviour of nitrile rubber (NBR)/poly(ethylene-co-vinyl acetate) (EVA) blends was studied by thermogravimetry. The effects of blend ratio, different crosslinking systems (sulphur, peroxide and mixed), various fillers (silica, clay and carbon black) and filler loading on the thermal properties were evaluated. It was found that the initial decomposition temperature increased with the addition of NBR to EVA. Among the various crosslinking systems studied, the peroxide cured system showed the highest initial decomposition temperature. This is associated with the high bond dissociation energy of C–C linkages. The addition of fillers improved the thermal stability of the blend. The mass loss at different temperatures and activation energy of degradation were also studied. The thermal ageing of these blends was carried out at 50 and 100°C for 72 h. It was seen that the properties are not affected by the mild ageing condition. Also, the peroxide cured system was found to exhibit better retention in properties, than other crosslinking systems.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have