Abstract
The stability of selectively formed TiSi2 films on single crystal and polycrystalline silicon layers at elevated process temperatures is reported. Extensive electrical and analytical studies were performed to understand the high-temperature stability of TiSi2 films as a function of (i) substrate dopant concentration, (ii) titanium silicide thickness, (iii) silicide formation sequence, and (iv) silicide post-processing steps. It is shown that all four process variations have a profound influence on the thermal stability of TiSi2 films. It is observed that titanium silicide films formed on single crystal silicon are stable at higher processing temperatures compared to those formed on polysilicon substrates under similar conditions. The degradation of high-temperature stability of TiSi2 films on polycrystalline silicon can be related to increased number of defects and grain boundaries. It is shown that TiSi2 films can be successfully used in silicon integrated circuit applications where the post-silicide processing temperatures do not exceed 1000 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.