Abstract
Thermal properties differences between rigid rod tetramethyl biphenyl (TMBP) and flexible diglycidyl ethers of bisphenol A (DGEBA) epoxies were studied using modified differential scanning calorimeter (MDSC), thermogravimetric analyzer (TGA) and dynamic mechanical analyzer (DMA) techniques. These epoxies were cured with phthalic anhydride (PA) and phenolic resin (PF5110), respectively. The PF5110-cured epoxy has better thermal properties than the PA-cured epoxy with a higher glass transition temperature (Tg) and a higher decomposition temperature. The good thermal properties of the PF5110-cured epoxy are due to the rigid PF5110 structure on the cured epoxy. DGEBA epoxy has a higher decomposition temperature than the rigid rod epoxy when they are cured with PF5110. But, in the PA curing system, rigid rod epoxy has a better thermal stability. These two different results are due to the different structures of curing agents.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.