Abstract
Chitosan can readily dissolve in a precooled aqueous alkali-urea solution, a solvent that has previously been developed to dissolve cellulose. Upon heating, the resulting solutions quickly become a gel. The thermal gelling of the chitosan solutions was studied by rheology. Initially, a temperature ramp test was used to determine the gelation temperatures (Tgel). It was found that Tgel does not significantly change with chitosan concentration. The in situ formed gels liquefy on cooling, but the liquefication temperature (Tliq) is considerably lower than Tgel, indicating a large hysteresis in the cooling process. In addition, Tliq decreases with increasing polymer concentration. The kinetics of thermal gelation was then studied by isothermal curing. The solution gels were cured not only at temperatures above the Tgel, which was determined in the temperature ramp test, but also at temperatures far below the Tgel, provided that the solution is cured at the temperature for a long enough time. The solutions become gel faster when cured at higher temperatures. When cured at the same temperature, higher concentration solutions become gel faster. The apparent activation energy for the thermal gelation of the chitosan solutions was determined to be ∼200 kJ mol(-1). Physical gels of pure chitosan were obtained by repeated soaking the in situ formed gels in water. Preliminary test shows that new gels are highly biocompatible.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.