Abstract
Nanorods of bismuth sulphide were prepared by thermal decomposition of bismuth N-ethyl cyclohexyl dithiocarbamate at different calcination duration. X-ray diffraction (XRD) analysis shows that at 400°C, the precursor was fully decomposed to orthorhombic bismuth sulphide after 2h of calcination. Besides, calcination duration does not affect the existence of Bi2S3 phase. Field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM) analyses reveal that Bi2S3 nanorods with an average width ranging from 29–36nm were obtained. Energy dispersive X-ray (EDX) analysis confirmed the atomic ratio of Bi and S close to 2:3, giving a possible composition of Bi2S3. Direct band gap energy of Bi2S3 decreases from 1.83eV to 1.54eV as calcination time increases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.