Abstract
A nonstoichiometric La1.5Sr0.5Ga3O7.25 melilite oxide ion conductor features active interstitial oxygen defects in its pentagonal rings with high mobility. In this study, electron localization function calculated by density functional theory indicated that the interstitial oxide ions located in the pentagonal rings of gallate melilites may be removed and replaced by electron anions that are confined within the pentagonal rings, which would therefore convert the melilite interstitial oxide ion conductor into a zero-dimensional (0D) electride. The more active interstitial oxide ions, compared to the framework oxide ions, make the La1.5Sr0.5Ga3O7.25 melilite structure more reducible by CaH2 using topotactic reduction, in contrast to the hardly reducible nature of parent LaSrGa3O7. The topotactic reduction enhances the bulk electronic conduction (σ ∼ 0.003 S/cm at 400 °C) by ∼ 1 order of magnitude for La1.5Sr0.5Ga3O7.25. The oxygen loss in the melilite structure was verified and most likely took place on the active interstitial oxide ions. The identified confinement space for electronic anions in melilite interstitial oxide ion conductors presented here provides a strategy to access inorganic electrides from interstitial oxide ion conductor electrolytes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.