Abstract
AbstractIn this article, a weld line placed behind an obstacle in an injection‐molded plaque made of metallic mold‐in‐color polypropylene (PP) was investigated. A broad uneven glossy section was visually observed along the weld line after the v‐notch weld disappeared. Although disk‐shaped metallic pigments were oriented parallel to the wall according to laminar flow, the pigment particles at the weld behind the obstacle were ordered vertically at the center of the depth direction. In PP molded without pigment, a black line was observed at the same position in the metallic weld. Based on a measurement of the crystal structure, the black line was caused by the rapid cooling of molten PP. Elongational flow occurred along the weld line after the diminishing v‐notch weld. The unique flow ordered the pigments obliquely at the advancing flow front and disturbed the subsequent flow of hot PP which transferred heat to the crystallizing mass. POLYM. ENG. SCI., 2011. © 2010 Society of Plastics Engineers
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.