Abstract
In recent years intermetallic γ-TiAl based alloys with additional amounts of the ternary bcc β Ti(Al,Nb) phase attracted increasing attention due to their improved workability at elevated temperatures. Depending on alloy composition and heat treatment the ductile high-temperature β phase can transform to several ordered phases at lower temperatures. However, currently available phase diagrams of these multiphase alloys are quite uncertain and the precipitation kinetics of some metastable phases is far from understood. In the present study various transformation pathways of the third phase were observed in situ by means of high-energy X-ray diffraction using synchrotron radiation. A Ti-45Al-10Nb (at.%) specimen was subjected to a temperature ramp of repeated heating cycles (700 °C - 1100 °C) with subsequent quenching at different rates. Depending on the quenching rate reversible transformations of the B2-ordered βo phase to different ω-related phases were observed. The results indicate that the complete transformation from βo to hexagonal B82-ordered ωo consists of two steps which are both diffusion controlled but proceed with different velocities.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.